One of the most relevant events controlling fatigue crack propagation under fretting conditions is the steep stress gradient generated in the material by contact loads. This fact suggests that crack growth process may be analysed using methodologies similar to those used for notched components. The present work assesses the capability of some methods originally developed for notched components to predict the fatigue failure of fretted specimens with spherical contact. The effect of local variation in R-ratio along the crack path is taken into account. The predictions are compared with a number of experimental results obtained using specimens of Al-7075-T6 subjected to fretting fatigue with spherical contact.Uno de los aspectos principales que controlan el crecimiento de una grieta por fatiga bajo condiciones de fretting es el fuerte gradiente generado en el material por las cargas de contacto. Este hecho sugiere que el proceso de fatiga pueda ser analizado usando metodologías similares a las empleadas en componentes entallados. El presente trabajo analiza la capacidad que algunos métodos originariamente empleados en entallas tienen para predecir el fallo por fatiga de elementos sujetos a fretting con contacto esférico. El efecto de la variación de R a lo largo del plano de la grieta es tenido en cuenta y analizado con dichos modelos. Las predicciones se comparan con resultados experimentales obtenidos con probetas de Al-7075-T6 sujetas a fatiga por fretting con contacto esfera-plano.Ministerio de Ciencia y Tecnología PB97-0696-C02-01Ministerio de Ciencia y Tecnología DPI2001-239