CORE
🇺🇦
make metadata, not war
Services
Services overview
Explore all CORE services
Access to raw data
API
Dataset
FastSync
Content discovery
Recommender
Discovery
OAI identifiers
OAI Resolver
Managing content
Dashboard
Bespoke contracts
Consultancy services
Support us
Support us
Membership
Sponsorship
Community governance
Advisory Board
Board of supporters
Research network
About
About us
Our mission
Team
Blog
FAQs
Contact us
Comparison of an Experimental Bone Cement with a Commercial Control, Hydroset™
Authors
D. Boyd
O. M. Clarkin
S. Madigan
Mark R. Towler
Publication date
1 July 2009
Publisher
Scholars\u27 Mine
Abstract
Glass polyalkenoate cements based on strontium calcium zinc silicate glasses (Zn-GPCs) and high molecular weight polyacrylic acids (PAA) (MW; 52,000-210,000) have been shown to exhibit mechanical properties and in vitro bioactivity suitable for arthroplasty applications. Unfortunately, these formulations exhibit working times and setting times which are too short for invasive surgical applications such as bone void filling and fracture fixation. In this study, Zn-GPCs were formulated using a low molecular weight PAA (MW; 12,700) and a modifying agent, trisodium citrate dihydrate (TSC), with the aim of improving the rheological properties of Zn-GPCs. These novel formulations were then compared with commercial self-setting calcium phosphate cement, Hydroset™, in terms of compressive strength, biaxial flexural strength and Young\u27s modulus, as well as working time, setting time and injectability. The novel Zn-GPC formulations performed well, with prolonged mechanical strength (39 MPa, compression) greater than both vertebral bone (18.4 MPa) and the commercial control (14 MPa). However, working times (2 min) and rheological properties of Zn-GPCs, though improved, require further modifications prior to their use in minimally invasive surgical techniques. © 2009 Springer Science+Business Media, LLC
Similar works
Full text
Open in the Core reader
Download PDF
Available Versions
Missouri University of Science and Technology (Missouri S&T): Scholars' Mine
See this paper in CORE
Go to the repository landing page
Download from data provider
oai:scholarsmine.mst.edu:che_b...
Last time updated on 05/03/2023