CORE
🇺🇦
make metadata, not war
Services
Services overview
Explore all CORE services
Access to raw data
API
Dataset
FastSync
Content discovery
Recommender
Discovery
OAI identifiers
OAI Resolver
Managing content
Dashboard
Bespoke contracts
Consultancy services
Support us
Support us
Membership
Sponsorship
Community governance
Advisory Board
Board of supporters
Research network
About
About us
Our mission
Team
Blog
FAQs
Contact us
Comparison of Failure Mechanisms for Cements Used in Skeletal Luting Applications
Authors
D. Boyd
O. Clarkin
Mark R. Towler
Publication date
1 August 2009
Publisher
Scholars\u27 Mine
Abstract
Glass Polyalkenoate Cements (GPCs) based on strontium calcium zinc silicate (Sr-Ca-Zn-SiO2) glasses and low molecular weight poly (acrylic acid) (PAA) have been shown to exhibit suitable compressive strength (65 MPa) and flexural strength (14 MPa) for orthopaedic luting applications. In this study, two such GPC formulations, alongside two commercial cements (Simplex ® P and Hydroset™) were examined. Fracture toughness and tensile bond strength to sintered hydroxyapatite and a biomedical titanium alloy were examined. Fracture toughness of the commercial Poly(methyl methacrylate) cement, Simplex® P, (3.02 MPa m1/2) was superior to that of the novel GPC (0.36 MPa m1/2) and the commercial calcium phosphate cement, Hydroset™, for which no significant fracture toughness was obtained. However, tensile bond strengths of the novel GPCs (0.38 MPa), after a prolonged period (30 days), were observed to be superior to commercial controls (Simplex™ P: 0.07 MPa, Hydroset™: 0.16 MPa). © 2009 Springer Science+Business Media, LLC
Similar works
Full text
Open in the Core reader
Download PDF
Available Versions
Missouri University of Science and Technology (Missouri S&T): Scholars' Mine
See this paper in CORE
Go to the repository landing page
Download from data provider
oai:scholarsmine.mst.edu:che_b...
Last time updated on 05/03/2023