The spectral analysis of external magnetic field influence on hydrothermally synthesized CoFe2O4, FeFe2O4, and MgFe2O4 nanoparticles in ferrofluid was presented. In order to control particle growth, stabilize particles against aggregation and enhance dispersibility in an aqueous medium, surface coating was achieved using citric and oleic acid, popular surfactants in preparation of magnetic particles for medical applications. New experimental settings were developed for the study of behavior of ferrofluids with the applied magnetic field strength in the range of 30-400 mT. Field-induced change of transmittance occurred and a precipitation of all studied samples was obtained. Contrary to the linear aggregates of colloidal CoFe2O4 and FeFe2O4, approximately spherical aggregates were observed in the case of MgFe2O4. The behavior of this kind of ferrites is in accordance with its soft magnetic nature. In all cases, the surface modification resulted in decreased dipole-dipole interactions between magnetic cores, and consequentially less precipitates were noticed. All citrate coated nanoparticles have shown stronger magnetic response in comparison to the oleate modified samples. The aggregation of nanoparticles potentially increases cytotoxicity although it is still unknown how aggregates formed in external magnetic field affect biological responses when ferrites are used in biomedical applications. Regarding non-linear clustering of MgFe2O4 suspensions, it can be concluded that its excretion from the organism could be likely easier and faster when used in diagnosis and/or therapy. Therefore, more attention should be paid to the low toxic MgFe2O4 for its medical application