Commercial use of lead halide perovskites requires improved ther mal stability and therefore a better understanding of their degrada tion mechanisms. The thermal degradation of three clean perovskite single crystal surfaces MAPbI3, MAPbBr3, FAPbBr3 was investigated using synchrotron based photoelectron spectroscopy. Central find ings are that the halide has a large impact on thermal stability and that the degradation of formamidnium results in the formation of a new organic species at the FAPbBr3 crystal surfac