Abstract
Oxide-ceramic coatings during the process of Micro-Arc Oxidation (MAO) with nanoscale titanium nitride were modified, which allowed one to obtain oxide-nitride ceramics in the shape of a coating on an aluminum alloy D16. The highest concentration of titanium nitride was registered in the surface coating layers, and the modification area extended to 1/3 of its thickness. It was found that the modification was accompanied by a 1.2–1.4-fold increase in the microhardness that achieved 23 GPa. Tribological tests under boundary lubrication showed that the modification of the MAO-coating with titanium nitride reduced the friction coefficient by a factor of 1.5–2.8 as compared to an unmodified coating. In addition to improving anti-friction properties, the wear resistance of coatings increased by a factor of 3–5.Осуществлено модифицирование в процессе МДО оксидокерамических покрытий наноразмерным нитридом титана, что позволило получить оксидно-нитридную керамику в виде покрытия на алюминиевом сплаве Д16. Наибольшая концентрация нитрида титана регистрируется в поверхностных слоях покрытия, при этом область модифицирования распространена до 1/3 его толщины. Установлено, что модифицирование сопровождается повышением микротвердости в 1,2–1,4 раза, которая достигает 23 ГПа. Триботехнические испытания в условиях граничного трения показали, что модифицирование МДО-покрытий нитридом титана приводит к снижению коэффициента трения в 1,5–2,8 раз по сравнению с немодифицированным покрытием. Помимо повышения антифрикционных свойств, достигается повышение износостойкости покрытий в 3–5 раз