Abstract
The possibility of synthesis of metal-matrix composites via coprecipitation of nickel with the particles of МоО3 (core)–WO3(shell) structure was demonstrated. It has been shown that the deposition of WO3 shell permits one to stabilize the dispersed molybdenum trioxide in the nickel plating bath, with the particles of second phase retaining the redox activity that facilitates their overgrowing with matrix metal and ensures large oxide loading in the nickel deposit at a low concentration of oxide in the electrolyte. It is shown that due to the lamellar structure inherent in the MoO3 core the Ni–MoO3/WO3 composites exhibit enhanced wear resistance that is more than 3 times as high as that of bare galvanic nickel.Продемонстрирована возможность получения металл-матричных композитов за счет соосаждения никеля с частицами типа «ядро (МоО3)–оболочка (WO3)». Показано, что нанесение оболочек из триоксида вольфрама позволяет стабилизировать дисперсный триоксид молибдена в растворах электрохимического никелирования при сохранении частицами редокс-активности, что положительным образом сказывается на враста- нии частиц дисперсной фазы в металлическую матрицу и позволяет обеспечить высокое содержание оксида в никелевом покрытии при его небольшой концентрации в электролите. Показано, что благодаря слоистому строению частиц дисперсной фазы композиты Ni–MoO3/WO3 характеризуются высокими уровнями износостойкости (превышающим износостойкость гальванического никеля более чем в 3 раза)