CORE
🇺🇦
make metadata, not war
Services
Services overview
Explore all CORE services
Access to raw data
API
Dataset
FastSync
Content discovery
Recommender
Discovery
OAI identifiers
OAI Resolver
Managing content
Dashboard
Bespoke contracts
Consultancy services
Support us
Support us
Membership
Sponsorship
Community governance
Advisory Board
Board of supporters
Research network
About
About us
Our mission
Team
Blog
FAQs
Contact us
Experimental investigations on the correlations between the structure and thermal-electrochemical properties of over-discharged ternary/Si-C power batteries
Authors
Xuanzhuang Chen
Xin Ge
+7 more
Qiqiu Huang
Xinxi Li
Dan Shao
Hongwei Wu
Guoqing Zhang
Jiangyun Zhang
Zhicheng Zhen
Publication date
19 September 2021
Publisher
'Wiley'
Doi
Cite
Abstract
© 2021 John Wiley & Sons Ltd. This is the accepted manuscript version of an article which has been published in final form at https://doi.org/10.1002/er.7274The thermal safety of power lithium-ion batteries(LIBs) has seriously affected the booming development of electric vehicles (EVs). Especially, owing to the requirement of high energy density, thermal runaway (TR) easily occurs in LIBs, resulting in a higher heat generation rate. Over-discharging is recognized as a common cause for TR. In the present research, the correlations between the structure and thermal-electrochemical properties of an over-discharged ternary/Si-C battery at room and high temperatures were investigated. The heat generation mechanisms of the batteries due to the maximum surface temperature and peak temperature difference variations during fast charging and discharging processes were investigated. Moreover, the electrochemical performances parameters of the batteries, such as voltage changing trend, discharge time, discharge capacity, internal resistance, electrochemical impedance spectroscopy (EIS) spectra, were analyzed. When the battery was discharged at 2.0C and 55°C, its maximum temperature and highest temperature difference reached 91.34°C and 13.24°C, respectively, finally resulting in a sharp decline in electrochemical performance. Furthermore, the root reasons for performance degradation and heat generation intensification of the over-discharged battery (ODB) were analyzed by scanning electron microscopy (SEM) and X-ray diffraction (XRD). The cause of the aforementioned phenomenon is due to irreversible damage of the electrode materials. This research not only reveals the relevant relationship between the thermal behavior and the microscopic structure of the over-discharged ternary/Si-C battery under various temperature conditions but also provides valuable insights for improving the safety of LIBs modules even packs.Peer reviewe
Similar works
Full text
Open in the Core reader
Download PDF
Available Versions
University of Hertfordshire Research Archive
See this paper in CORE
Go to the repository landing page
Download from data provider
oai:uhra.herts.ac.uk:2299/2594...
Last time updated on 12/12/2022