High strength low alloy (HSLA) steel has higher mechanical strength than steel in general but with easy weldability, in this study the material used is S690QL. Flame straightening is used to restore the distorted shape of the S690QL material due to the heating and cooling process during the fabrication process. The purpose of this study was to determine the hardness value of the S690QL material after going through the flame straightening process. Flame straightening process is carried out by line heating technique using temperature variations of 700 °C, 750 °C, and 800 °C for 45 minutes in each temperature variant. A nozzle with a diameter of 14 mm – 20 mm with a multi flame torch is used in the flame straightening process. As a step to reduce residual stress and stress relieving, Post Weld Heat Treatment (PWHT) with a holding time of 1 hour was carried out. The process is continued with water cooling to room temperature. Vickers hardness test is carried out by taking 9 sample points, 2 points on the base metal, and 7 points on the Heat Affected Zone area. Based on the test results, it is known that at temperatures of 700 and 750 there has been no phase change, so the highest hardness values at these temperatures are 270 HVN and 295 HVN. While at a temperature of 800 °C, there was a phase change marked by the hardness value which increased to 379 HVN.Baja high strength low alloy (HSLA) memiliki kekuatan mekanis lebih tinggi dibanding baja pada umumnya tetapi dengan weldability yang mudah, dalam studi ini material yang dipakai adalah S690QL. Flame straightening digunakan untuk mengembalikan bentuk material S690QL yang telah terdistorsi akibat proses pemanasan dan pendinginan selama proses fabrikasi. Tujuan penelitian ini adalah untuk mengetahui nilai kekerasan material S690QL setelah melalui proses flame straightening. Proses Flame straightening dilakukan dengan teknik line heating menggunakan variasi suhu 700 °C, 750 °C, dan 800 °C selama 45 menit di setiap varian suhu. Nozzle dengan diameter 14 mm – 20 mm dengan multi flame torch digunakan dalam proses flame straightening. Sebagai langkah pengurangan tegangan sisa dan stress relieving, Post Weld Heat Treatment (PWHT) dengan holding time 1 jam dilakukan. Proses dilanjutkan dengan air cooling hingga temperatur ruang. Pengujian kekerasan Vickers dilakukan dengan pengambilan 9 sampel titik, 2 titik pada bagian base metal, dan 7 titik pada area Heat Affected Zone. Berdasarkan hasil pengujian diketahui bahwa pada suhu 700 °C dan 750 °C belum terjadi perubahan fasa, sehingga nilai kekerasan tertinggi pada suhu tersebut adalah 270 HVN dan 295 HVN. Sedangkan pada suhu 800 °C, terjadi perubahan fasa ditandai dengan nilai kekerasan yang meningkat menjadi 379 HVN