Wpływ starzenia na strukturę i właściwości termiczne kompozytów polimerowych z włóknem tekturowym

Abstract

In this work the results of investigations of thermal properties and structure PE-HD with addition of cardboard fibre before and after UV radiation ageing were presented. In this work composites with content of 1, 3, 5% of cardboard fibre in relation to the polyethylene have been produced. The investigations for the influence of the fillers on the properties of prepared composites before and after ultraviolet radiation ageing have been conducted. Investigations of crystallinity degree by means of DSC method as well as investigations of the structure using optical microscope have been conducted. The DSC investigations prove the decrease in the crystallinity degree of PE-HD during addition of cardboard fibre and increase for the samples after ultraviolet radiation ageing. While increasing the amount of cardboard fibre in the composite the Vicat softening temperature and absorptivity of water decreases for the samples before ultraviolet radiation ageing.W pracy przedstawiono wyniki badań właściwości termicznych oraz struktury polietylenu o dużej gęstości i kompozytów polietylenu z włóknem tekturowym przed i po procesie starzenia promieniami UV. Zbadano stopień krystaliczności metodą DSC oraz strukturę za pomocą mikroskopu optycznego w świetle przechodzącym. Określono również temperaturę mięknienia wg Vicata oraz chłonność wody. Badaniom poddano kompozyty polietylenu o zawartości włókna: 1, 3 i 5%. Stwierdzono wpływ napełniacza na stopień krystaliczności, którego wartość maleje ze wzrostem zawartości włókna tekturowego zarówno przed, jak i po starzeniu promieniami UV. W przeprowadzonych badaniach zarejestrowano niższe wartości temperatury mięknienia wg Vicata i większą chłonność wody dla kompozytów polietylenu z włóknem tekturowym po starzeniu promieniami UV