Wpływ swobodnej energii powierzchniowej na właściwości tribologiczne warstw tlenkowych wytwarzanych na stopie aluminium EN AW-5251

Abstract

This paper presents the influence of the parameters of the formation of oxide layers on the surface free energy and the tribological properties of these layers. The layers were formed electrochemically on aluminium alloy EN AW-5251, with variable values of electrolyte temperature and current density. A three-component electrolyte was used to produce oxide layers. The surface free energy was determined by the droplet deposition method by measuring the wetting angles, while the van Oss-Chaunhury-Good method was used for the calculations. Tribological tests were performed on a T-17 tribological tester under conditions of technically dry friction for reciprocating motion. T7W composite was used as a specimen in tribological tests.W artykule przedstawiono wpływ parametrów wytwarzania warstw tlenkowych na swobodną energię powierzchniową oraz właściwości tribologiczne tych warstw. Warstwy zostały wytworzone na stopie aluminium EN AW-5251 metodą elektrochemiczną, przy zmiennych wartościach temperatury elektrolitu oraz gęstości prądowej. Do wytwarzania warstw tlenkowych zastosowano elektrolit trójskładnikowy. Swobodna energia powierzchniowa wyznaczona została metodą osadzonej kropli poprzez pomiar kątów zwilżania, natomiast do obliczeń zastosowano metodę van Ossa-Chaunhury’ego-Gooda. Testy tribologiczne przeprowadzono na testerze tribologicznym T-17 w warunkach tarcia technicznie suchego dla ruchu posuwisto-zwrotnego. W testach tribologicznych jako próbki użyto kompozytu T7W