Porównanie wpływu procesu druku 3D oraz procesu wtryskiwania na właściwości tribologiczne polilaktyd (PLA)

Abstract

This article presents the results of studies on the tribological properties of linear wear and kinetic friction of polylactide processed by 3D printing (FFF) and injection moulding. Research was conducted on a pin on disc apparatus, and the test specimens used were polylactide cylinders with the counter specimen of C45 steel disc. Research was planned and executed with the planned experiment method for two variables: velocity of the counter specimen and pressure. The range of specified values was in the following sections: p = (0.2;0.6) MPa and v = (0.2;1.0) m/s . The conducted experiment had a target of defining the influence of a somewhat new method of 3D printing on the tribological properties of materials that might find application in prototyping plain bearings.W niniejszej pracy przedstawiono wyniki badań właściwości tribologicznych: zużycia liniowego oraz tarci kinetycznego dla polilaktydu przetworzonego w procesie druku 3D (FFF) oraz w procesie wtryskiwania. Badania przeprowadzone zostały na aparaturze pin on disc, próbkę stanowił materiał badany, przeciwpróbkę – tarcza stalowa C45. Badania zostały zaplanowane i przeprowadzone przy pomocy eksperymentu rotalnego dla dwóch zmiennych – prędkości obrotowej tarczy stalowej oraz nacisku. Zakres określonych wartości zawierał się w przedziałach: p = (0.2;0.6) MPa and v = (0.2;1.0) m/s . Przeprowadzony eksperyment miał na celu przedstawienie wpływu stosunkowo nowej metody druku 3D na właściwości tworzyw sztucznych, mogących znaleźć zastosowanie w wytwarzaniu prototypowych lub krótkobieżnych łożysk ślizgowych