In this work, a composite nanomaterial consisting of graphene (Gr), double-wall carbon nanotube (DWCNTs) and gold nanoparticles (AuNPs), designated as DWCNTs-AuNPs-Gr was synthesized via the thermal chemical vapour deposition technique. The morphology and electrical and electrochemical properties of the material were characteried by using field emission scanning electron microscopy, Raman spectroscopy, four-probe sheet resistance measurement, and cyclic voltammetry (CV). The average sheet resistance value of DWCNTs-AuNPs-Gr is 549 W/sq, 2.3 times lower than that of graphene. The current response of a DWCNTs-AuNPs-Gr-modified electrode in a 2 mM K3[Fe(CN)6]/K4[Fe(CN)6] solution with 0.1 M PBS is 15.79 µA, 1.48 times higher than that of a graphene-modified electrode and 2.57 times higher than that of a bare electrode. The DWCNTs-AuNPs-Gr material can be used for electrochemical biosensors to detect various bioelements.Trong công trình này, màng tổ hợp của vật liệu graphene (Gr) – ống nano cácbon hai tường (DWCNT) và hạt nano kim loại vàng (AuNPs) (DWCNT-AuNPs-Gr) đã được chế tạo bằng phương pháp lắng đọng pha hơi nhiệt hóa học (CVD). Hình thái học bề mặt và các tính chất điện, điện hóa của vật liệu tổ hợp đã được khảo sát thông qua kính hiển vi điện tử quét phát xạ trường, phổ Raman, điện trở bốn mũi dò và kỹ thuật quét thế vòng (CV). Với nồng độ DWCNTs 0,3 g/L và tốc độ quay phủ 4000 vòng/phút, vật liệu DWCNTs-AuNPs-Gr có điện trở bề mặt giảm 2,3 lần so với màng Gr và đạt khoảng 549 W/sq; dòng đỉnh đáp ứng trong dung dịch 2 mM K3[Fe(CN)6]/K4[Fe(CN)6] trong 0,1 M PBS đạt 15,79 µA tại 50 mV/s, cao gấp 1,48 lần so với điện cực biến tính màng Gr và gấp 2,57 lần so với điện cực trần. Vật liệu DWCNTs-AuNPs-Gr có tiềm năng ứng dụng trong cảm biến điện hóa để phát hiện các phần tử sinh học khác nhau