Abstract
Sr1-xGdxFe12-xCoxO19 ( x = 0; 0.1; 0.2; 0.3; 0.4; 0.5) ferrites have been prepared by solid-state method under air at 1473 K. It has been found that increasing the value of x first leads to a slight decrease in the Curie temperature, from 727 K for the base ferrite SrFe12O19 to 725 K of solid solution Sr0.9Gd0.1Fe11.9Co0.1O19, but with x further increasing, the Curie temperature rises reaching 745 K at x=0.5. It has been found that at 5 K and 300 K, spontaneous magnetization (no) values are respectively 4.2 and 3.7 % higher for solid solution Sr0.9Gd0.1Fe11.9Co0.1O19 than for the base ferrite SrFe12O19.Твердофазным методом на воздухе при температуре 1473 K получены образцы ферритов Sr1-xGdxFe12-xCoxO19 ( x = 0; 0,1; 0,2; 0,3; 0,4; 0,5). Рентгенофазовый анализ показал, что образцы с x≥0,2, кроме основной фазы со структурой магнетоплюмбита, содержали примесные фазы α-Fe2O3, Gd3Fe5O12, в образцах с x=0,3; 0,4; 0,5 присутствовали фазы GdFeO3, CoFe2O4, а в образцах с x=0,4; 0,5 - фаза Gd2O3. Установлено, что увеличение параметра состава x сначала приводит к незначительному уменьшению температуры Кюри от 727 K для SrFe12O19 до 725 K для феррита с x=0,1, а при дальнейшем увеличении x до 0,5 она немного возрастает и для образцов с x=0,5 составляет 745 K. Установлено, что твердый раствор феррита Sr1-xGdxFe12-xCoxO19 с x=0,1 при 5 и 300 K имеет значения самопроизвольной намагниченности (и0) больше, чем у феррита SrFe12O19 на 4,2 и 3,7 % соответственно