The article describes the microstructure and the technological properties of a direct quenched ultrahighstrength strip steel with the minimum specific yield strength of 1100MPa. The microstructure of thislow carbon, Mn-Cr-Mo-Cu-Ni alloyed steel consists mainly of auto-tempered lath martensite. Due to thesophisticated thermo-mechanical controlled processing schedule, the martensite transformation takesplace from a fine and uniform austenite grain structure. State-of-the-art steelmaking and continuous castingoperations guarantee a good inclusion cleanness and low level of segregation. The steel has excellent impactand fracture toughness properties with respect to its ultra-high strength level. The determined transitiontemperature for 28J in Charpy-V test and fracture toughness characteristic temperature, T0, were below-100°C. The weldability tests indicated that the impact toughness of the heat affected zone (HAZ) is excellentand there is no significant softening in the HAZ or in the welded joint in the wide range of t8/5 cooling times.The steel allows crack-free bending with a minimum inside bending radius equal to 3 times material thicknessirrespective of the bending direction. In addition, the steel has a good resistance to atmospheric corrosion