MIREA – Russian Technological University (RTU MIREA).
Abstract
Dielectric properties of single crystals of LiNbGeO5, crystallizing in the andalusite (β-Al2SiO5) structure, have been studied. Dielectric and conducting properties along the major crystallographic axes were investigated at frequencies from 1 to 1000 kHz and in the range of temperatures between 100 and 600 K. Determined potential barriers between the equilibrium positions of Li+ ions are classified as low energy (0.23-0.79 eV, along the a axis) and high energy (0.9-1.90 eV, along the a, b, and c axes). Additional interstitial sites with the distances between them 0.3-0.4 Å have been found along the a axis, while no such sites observed along the b and c axes. Activation energy (Ea) in the direction a is 0.47 eV and ?a(570 K) = 2.10-5 S/cm, which correspond to the super-ionic conductivity.Исследованы диэлектрические свойства монокристаллов LiNbGeO5 со структурой минерала андалузита (β-Al2SiO5). Диэлектрические и проводящие свойства изучены вдоль главных кристаллографических осей a, b, c при частоте измерительного поля 1-1000 кГц в интервале температур 100-600 К. Найденные значения потенциальных барьеров между положениями равновесия ионов Li+ подразделяются на низкоэнергетические (0.23-0.79 эВ, a-ось) и высокоэнергетические (0.9-1.80 эВ, a, b и c-оси). В направлении оси a обнаружены дополнительные междуузельные позиции с расстояниями между ними 0.3-0.4 A, в то время как для осей b и c такие позиции отсутствуют. В направлении a энергия активации Еa = 0.47 эВ и значение ?a(570 К) = 2.10-5 См/см, что соответствует суперионной проводимости