MIREA – Russian Technological University (RTU MIREA).
Abstract
Some properties of lithium-indium complex phosphates in the previously investigated Li3PO4-Na3PO4-InPO4 ternary system were studied. Ionic conductivity of isolated phases at 300ºC was measured. Vibration spectra of the investigated compounds were registered for 6Li → 7Li substituted samples from 1400 to 200 cm-1 frequency range. Isotope shifts under 6Li → 7Li substitution were observed for all the complex phosphates. The obtained results allowed to reveal intrinsic lithium sublattice vibration and to relate complex phosphates structure to ionic conductivity magnitude.Изучены некоторые свойства сложных фосфатов лития и индия, выделенных в ранее исследованной системе Li3PO4-Na3PO4-InPO4. Определена ионная проводимость выделенных фаз при 300ºC. Kолебательные спектры исследуемых соединений были зарегистрированы для 6Li → 7Li изотопозамещенных образцов, в частотном диапазоне от 1400 до 200 см-1. Изотопные сдвиги частот отмечены для каждого исследуемого сложного фосфата, что позволило выявить собственные колебания подрешетки лития и установить взаимосвязь между структурой сложных фосфатов и величиной ионной проводимости
