The effects of atmospheric pressure plasma treatment on wool fabric were tested in this study. A Diffuse Coplanar Surface Barrier Discharge (DCSBD) has been used. The operating frequency was 15 kHz, the power input 300 W. Wool fabric has been exposed by different times. Changes of fibres surface were characterized by means of XPS, FTIR spectroscopy and AFM methods. With the maximal experimental attention was observed dye sorption. Wool fabrics were dyed in dye bath by common used acid hydrophilic dyestuffs. As criterions dye sorption on wool were stated dyeing rate and dye uptake on wool fibres. Printing of wool by acid dyestuffs was carried out as well.KAN [101630651

Chvalinová, Radka

Wiener, Jakub

DSpace@TUL

Chem. Listy 102, s1473−s1477 (2008)                                                   II Central European Symposium on Plasma Chemistry 2008  s1473 SORPTION PROPERTIES OF WOOL  FIBRES AFTER PLASMA TREATMENT  RADKA CHVALINOVÁ and JAKUB WIENER  Department of Textile Chemistry, Textile Faculty, Technical University of Liberec, Studentská 2, 461 17  Liberec, Czech Republic radka.chvalinova@tul.cz, jakub.wiener@tul.cz   Introduction  The wool fibre exhibits a typical core − shell structure consisting of an inner protein core, cortex, and surface shell, cuticle1 (see Fig. 1). The cuticle consists of several lay-ers (see Fig. 2).  The upper layer, epicuticle, contains lipoproteins. Lipoid part of lipoproteins is bound by the sulfoester bond with pro-teinous part (see Fig. 3). Covalent bonds of branched chain fatty acids implicate hydrophobic character of wool fibres. The lipoproteins are connected with upper layer of exocuticle. Exocuticle is cross-linked by disulfide links (see Fig. 4).  The hydrophobic nature of the cuticle and the high cross-linking density in the outermost fibre surface creates a nature diffusion barrier2, which influences sorption proper-ties complicates wool finishing processes, such as printing, dyeing or shrink-proofing. Surface modification plays an important role for many chemical finishing processes in tex-tile industry.  The required surface modification is mainly accom-plished by wet chemical processes using special auxiliaries which attack the cuticle by hard chemicals as for example NaClO3,4.    Experiments  The effects of atmospheric pressure plasma treatment on wool fabric were tested in this study.  A Diffuse Coplanar Surface Barrier Discharge (DCSBD) has been used (see Fig. 5).  The operating frequency was 15 kHz, the power input 300 W. Wool fabric has been exposed by different times. Pure wool fabric has been exposed to different intensive plasma-treatment (different exposure times at constant conditions).  A conventionally-finished, plain-weave pure wool fabric (222 g m−2 manufactured from yarn of 2×19 tex) was used.   cortex cells   cuticle, scales Fig. 1. Structure of wool fibres3    Fig. 2. Schema of  cuticle4 PROTEIN LIPID EPICUTICLE Fig. 3. Lipoproteins in epicuticle Fig. 4. Stary`s wool fiber model6  Fig. 5. Used equipment DCSBD Plasma-chemical box Ceramic electrode Moving cart  Oil pump Ventilator Vacuum air pump HV convertor HV generator Moving cart power supply Chem. Listy 102, s1473−s1477 (2008)                                                   II Central European Symposium on Plasma Chemistry 2008  s1474 Dyeing of wool fabrics  Wool samples were pretreated by plasma for time 10, 20, 30, 50 and 100 seconds.  Untreated and plasma treated wool materials were dyed isothermal by acid dye (Colour Index Acid Yellow 42  − see Fig. 6) in weak acid solution (pH 6) at the temperature 60 °C (respectively 80 °C) for 2, 10 and similarly for 60 minutes. The dye bath contained 2 % dye of sample weight. After dye-ing, the dyed fabrics were rinsed with cold water for 5 min-utes. Dry dyed materials were measured by spectrophotome-ter Datacolor 3890 (Datacolor, Switzerland). As results of measurement were achieved remission values. The remissions R were by the using of well known Kubelka-Munk equation recalculated to the K/S values.  Printing of wool fabrics      Wool fabrics (untreated and plasma treated for 10, 50, 100 seconds) were printed by a printing paste (pH 6) with acid dye (C. I. Acid Yellow 42). Printed wool fabrics were fixed for 1, 3, 6 and 10 minutes at 60 °C. Samples were by this fixation wet – evaporation of water was eliminated. Along the aftertreatment were realized the rinsing with cold water for 5 minutes, the soaping at 40 °C with 2 g l−1 Synta-pon ABA for 10 minutes and the last rinsing with cold water for 5 minutes. The dyed wool materials were measured by spectrophotometer Datacolor 3890.  Visualization of surface structure  The structure and the appearance of fibres surfaces were observed with using of Scanning Electron Microscopy (SEM) on device VEGA (see Fig. 7). All the samples were coating by Gold before SEM testing. The structure of surface was observed by the means of microscopic method Atomic Force Microscopy (AFM). AFM is the method used for characterization of prepared sub-micron optical elements.  The method to describe changes of chemical bonds and formation of new chemical groups after the plasma treatment was used Fourier Transform Infrared Spectroscopy (FTIR) Spectrometer One (Perkin Elmer – ATR technique on ZnSe crystals).  Next it was used method X-ray Photoelectron Spectros-copy (XPS). The XPS technique is highly surface specific due to the short range of the photoelectrons that are excited from the solid. The energy of the photoelectrons leaving the sample gives a spectrum with a series of photoelectron peaks. The binding energy of the peaks is characteristic of each element. The measurements were preceded with the using apparatus ESCA PROBE P (Omicron Nanotechnology Ltd) in ultra-high vacuum (under pressure order 10−10 mbar). X-rays emit-ter is aluminium electrode (used energy 1486.7eV). Measured spectra were analysed by way of CasaXPS programme.   Results  Results of wool dyeing  The K/S values are the observed shade-area directly proportional to dye concentration in fibres. In Fig. 8 there are marked differences in sorption properties untreated and plasma treated wool dyed at 60 °C. The dye concentration increases with dye time and plasma treatment intensity. The plasma treatment for 10 second is exactly insufficient. The best dye sorption is obtained by plasma treated wool fabric for longest time (100 second).  NNNNSSNNNNO-O-OOOOOOCH3CH3Na+Na+Fig. 6. The chemical structure of acid dye with Colour Index              Acid Yellow 42 Fig. 7. Environmental scanning electron microscope Vega TS 5130 01230 10 20 30 40 50 60 time of dyeing [s]K/S value [-] plasma untreatedplasma treated 10 splasma treated 20 splasma treated 30 splasma treated 50 splasma treated 100 sDyeing of wool at 60°Cmin] Fig. 8. The influence of dyeing time on K/S values. Dyed at 60 °C Chem. Listy 102, s1473−s1477 (2008)                                                   II Central European Symposium on Plasma Chemistry 2008  s1475    Results of wool printing  Fig. 9 shows faster dye sorption and higher K/S values for dyeing of wool at 80 °C. The plasma treatment time 10 seconds doesn’t return sufficient results. These K/S values are the same as K/S values of untreated wool. The plasma treated wool fabric for 100 seconds sorbs double more dye than un-treated wool fabric. The similar results were stated in printing experiments.  The untreated wool fabric absorbs double under dye concentration than wool fabric which was plasma treated for 100 second (see Fig. 10).   Visualization of surface structure − results  SEM was used for visualization of surface structure wool fibers − epicuticle.   They were observed changes of surface wool scales. In Fig. 11–14 we can see invasion of structure of wool scales and breaking off their parts by the influence of plasma treat-ment.  By the using of method AFM, it visualized disturbs of epicuticle scales by plasma treatment.  In Fig. 15 and fig. 16 we can see evident differences between surfaces untreated and plasma treated wool fibres. By means of the FTIR were proved minor changes of wool chemical structure (see Fig. 17).  From results of the XPS it is obvious that it achieved Dyeing of wool at 80°C024681012140 10 20 30 40 50 60 time of dyeing [s]K/S value [-] plasma untreatedplasma treated 10 splasma treated 20 splasma treated 30 splasma treated 50 splasma treated 100 sFig. 9. The influence of dyeing time on K/S values. Dyed at 80 °C min] Fig. 10. The influence of fixation time on K/S values.  Fixed at 60 °C Printing of wool, fixation at 60°C01230 1 2 3 4 5 6 7 8 9 10 time of fixation [s]K/S value [-]plasma untreatedplasma treated 10 splasma treated 50 splasma treated 100 s[min] Fig. 11. Untreated wool Fig. 12. Plasma treated wool  for 10 s Fig. 13. Plasma treated wool  for 50 s Fig. 14. Plasma treated wool       for 100 s  6065707580859095100700120017002200270032003700vawe number [cm-1]transmitance [%]untreated plasma treated 10 s plasma treated 20 splasma treated 30 s plasma treated 50 s plasma treated 100 sFig. 17. FT-IR spectrum of wool fibers Fig. 15. Unterated wool fibres  Fig. 16. Plasma treated wool  fibres for 100 s Chem. Listy 102, s1473−s1477 (2008)                                                   II Central European Symposium on Plasma Chemistry 2008  s1476 changes of chemical structure on surface epicuticle. The con-centrations of oxygen increased after plasma treatment of wool fabric. The concentrations of nitrogen increased for 10 second plasma treatment and decreased for 100 seconds plasma treated wool fabric (see Table I).  There were stated the relative atomic ratios O/C and N/C. It was found the increasing the relative atomic ratios O/C and N/C. Surface oxidation is possible due to the existence of reactive species from the plasma. In Fig. 16–18 are showed surveillance spectrums untreated and plasma treated wool fibres.   Conclusion  Experiments showed invasion of surface layer of cuticle by plasma. Plasma treatment wool adsorbs dye more intensive at lower temperature. Plasma treatment of wool can in future replace wet pre-treatment processes for wool dyeing and wool printing. The pre-treatment of wool with atmospheric plasma give an appropriate environmentally acceptable alternative to conventional treatments.  This research has been supported by KAN 101630651.  REFERENCES   1.  Naebe M., Rippon J. A., Brady P. R., Wang X. G., Brack1 N., Riessen1 G. Van, Cookson P. G.: 6th Interna-tional Conference - TEXSCI 07, 2007.   2. Thomas T., (Shishoo R., ed.), p. 228. Woodhead Publish-Table I Relative chemical composition ratios determined by XPS for wool fabric Condition  C1s O1s N1s Untreated wool 76,2 13,7 8,0 Plasma treated 10 s 67,6 19,3 9,4 Plasma treated 100 s 57,6 32,1 8,1 Chemical composition [%]  Table II Relative atomic ratios determined by XPS for wool fabric Condition  O/C N/C Untreated wool 18,0 10,5 Plasma treated 10 s 28,5 14,0 Plasma treated 100 s 55,6 14,1 Atomic ratio [%]  Fig. 18. Surveillance spectrum of untreated wool Fig. 19. Surveillance spectrum of plasma treated wool for 10 s  Fig. 20. Surveillance spectrum of plasma treated wool for 100 s Chem. Listy 102, s1473−s1477 (2008)                                                   II Central European Symposium on Plasma Chemistry 2008  s1477 ing Limited, Cambridge 2007.    3. Lewis D. M.: Wool dyeing, Society of Dyers and Colour-ists, Leeds 1992.   4. Feldtman H. D., Leeder J. D., Rippon J. A, (R. Postle, S. Kawabata, M. Niwa, ed.) Osaka: Text. Mach. Soc. Japan, 1983, 125.   5. Jones N.: Hair Structure Anatomy and Comparative Anatomy, 98. Elsevier Science, New York 2001.    6. Rouette H. K.: Encyclopedia of Textile Finishing, Springer, New York 2001.   7. Höcker H.: Int. Text. Bull. Veredlung 41, 18 (1995).  R. Chvalinová and J. Wiener (Department of Textile Chemistry, Textile Faculty, Technical University of Liberec, Liberec, Czech Republic): Sorption Properties of Wool Fi-bres after Plasma Treatment  The effects of atmospheric pressure plasma treatment on wool fabric were tested in this study. A Diffuse Coplanar Surface Barrier Discharge (DCSBD) has been used. The operating frequency was 15 kHz, the power input 300 W. Wool fabric has been exposed by different times.  Changes of fibres surface were characterized by means of XPS, FTIR spectroscopy and AFM methods. With the maximal experimental attention was observed dye sorption. Wool fabrics were dyed in dye bath by common used acid hydrophilic dyestuffs. As criterions dye sorption on wool were stated dyeing rate and dye uptake on wool fibres. Print-ing of wool by acid dyestuffs was carried out as well.   

Sorption Properties Of Wool Fibres After Plasma Treatment

https://dspace.tul.cz/bitstream/15240/16350/1/208452600038-o.pdf

Sorption Properties Of Wool Fibres After Plasma Treatment

Abstract