CORE
🇺🇦
make metadata, not war
Services
Services overview
Explore all CORE services
Access to raw data
API
Dataset
FastSync
Content discovery
Recommender
Discovery
OAI identifiers
OAI Resolver
Managing content
Dashboard
Bespoke contracts
Consultancy services
Support us
Support us
Membership
Sponsorship
Community governance
Advisory Board
Board of supporters
Research network
About
About us
Our mission
Team
Blog
FAQs
Contact us
Structural stability of clean and passivated nanodiamonds having ledge, step, or corner features
Authors
Akberova N.
Alisheva D.
+3 more
Freitas R.
Izotova E.
Tarasov D.
Publication date
1 January 2012
Publisher
Abstract
The use of precisely applied mechanical forces to induce site-specific chemical transformations is called positional mechanosynthesis, and diamond is an important early target for achieving mechanosynthesis experimentally. The next major experimental milestone may be the mechanosynthetic fabrication of atomically precise 3D structures, creating readily accessible diamond-based nanomechanical components engineered to form desired architectures possessing superlative mechanical strength, stiffness, and strength-to-weight ratio. To help motivate this future experimental work, the present paper addresses the basic stability of nanoscale diamond structures with clean or hydrogenated surfaces that possess certain simple features including ledges, steps, and corners. Computational studies using Density Functional Theory (DFT) with the Car-Parrinello Molecular Dynamics (CPMD) code, consuming~2,284,108.97 CPU-hours of runtime on the IBM Blue Gene/P supercomputer (23 TFlops), confirm that fully hydrogenated nanodiamonds 1-2 nm in size possessing ledges with various combinations of convex or concave edgelines where any two of the three principal diamond faces meet will maintain stable sp 3 hybridization. © 2012 American Scientific Publishers. All rights reserved
Similar works
Full text
Open in the Core reader
Download PDF
Available Versions
Kazan Federal University Digital Repository
See this paper in CORE
Go to the repository landing page
Download from data provider
oai:dspace.kpfu.ru:net/139354
Last time updated on 07/05/2019