CORE
🇺🇦
make metadata, not war
Services
Services overview
Explore all CORE services
Access to raw data
API
Dataset
FastSync
Content discovery
Recommender
Discovery
OAI identifiers
OAI Resolver
Managing content
Dashboard
Bespoke contracts
Consultancy services
Support us
Support us
Membership
Sponsorship
Community governance
Advisory Board
Board of supporters
Research network
About
About us
Our mission
Team
Blog
FAQs
Contact us
Effects of microstructures on fatigue behavior of an Al-Mg-Sc alloy at an elevated temperature
Authors
Monzen Ryoichi
Watanabe Chihiro
Publication date
1 January 2012
Publisher
'Trans Tech Publications, Ltd.'
Doi
Cite
Abstract
Polycrystalline Al-1wt%Mg-0.27wt%Sc alloys bearing Al3Sc particles with different average sizes of 4 and 11nm Polycrystalline Al-1wt%Mg-0.27wt%Sc alloys bearing Al3Sc particles with different average sizes of 4 and 11nm in diameter have been cyclically deformed at 423K under various constant stress amplitudes, and the relationship between fatigue characteristics and microstructure of the alloy has been investigated. The specimen bearing 11 nm particles exhibited a cyclic hardening to saturation, while in specimens with the small particles a cyclic softening was observed after initial hardening. In the specimen with large particles, dislocations were uniformly distributed under all applied stress amplitudes, whereas the specimens bearing small particles, in which cyclic softening occurred exhibited clearly developed slip bands. The cyclic softening for the latter specimen was explained by particle shearing within the strongly strained slip bands. The width of precipitate free zones (PFZs) has been found to be one of the factors affecting the fatigue life of the specimens at 423K. The two-step aging decreases the width of PFZs, resulting in increase in the fatigue life. © 2012 Trans Tech Publications, Switzerland
Similar works
Full text
Open in the Core reader
Download PDF
Available Versions
Kanazawa University Repository for Academic Resources
See this paper in CORE
Go to the repository landing page
Download from data provider
oai:kanazawa-u.repo.nii.ac.jp:...
Last time updated on 06/05/2019