Fifteen-layered graphene films have been successfully deposited onto flexible substrates using a commercial ink consisting of graphene particles dispersed in an acrylic polymer binder. A value of 74.9 × 105cm−2 was obtained for the density of defects, primarily located at the flake edges, from the ratio of the D and G Raman peaks located at 1345cm1 and 1575cm1 respectively. 0.5μm thick drop-cast films on interdigitated silver electrodes exhibited Ohmic conduction with a small activation energy of 12meV over the temperature range from 260K to 330K . The photo-thermoelectric effect is believed to be responsible for photoconduction through graphene films under illumination intensity of 10mWm-2 at 270 nm, corresponding to the UV absorption peak. The photo-transient decay at the bias of 1V involves two relaxation processes when the illumination is switched off and values of 8.9 × 103 and 4.3 × 104 are found for the relaxation time constant using the Kohlrauch stretched exponential function analysis.Dr. Indrani Banerjee is grateful to Commonwealth Association, UK for funding the present research work under the fellowship placement scheme (Grant reference INCF-2014-66). The studentship of Ms Faris is partially sponsored by the Air Force Office of Scientific Research, Air Force Material Command, USAF, under Grant No. FA9550-15-1-0123. We are also thankful to Miss V. M. Torrejon of Brunel University for support in computer graphics