Characterization of Polyamide 66 membranes prepared by phase inversion using formic acid and hydrochloric acid such as solvents

Abstract

The membranes properties prepared from water/formic acid (FA)/ polyamide 66 (PA66) and water/hydrochloric acid (HCl)/polyamide 66 (PA 66) systems has been studied. The different solvents interact distinctly with the polymer, affecting the membrane morphology. The asymmetric structure of the membranes showed a dense top layer and a porous sublayer. The membranes M-HCl prepared from HCl/PA 66 system showed a larger dense layer (around 23 μm) in compared to those prepared from FA/PA 66 system (M-FA) (around 10 μm). The membrane morphology was a determinant factor in results of water absorption, porosity and pure water flux. The lower thickness of dense layer in M-FA membranes resulted in a higher water absorption and, consequently, porosity, approximately 50%, compared with M-HCl membranes, approximately 15%. The same trend was observed to permeate flux, the lower thickness of dense layer higher pure water flux