Centreline formation of Nb(C, N) eutectic in structural steel

Abstract

The reduction of area in the through thickness direction is an essential mechanical property of thick steel heavy plates. By a routine control, a very small through thickness reduction of area was found for tensile specimen of a 90 mm plate. Careful investigations of the fracture and section of specimens cut from the as solidified continuously cast 250mmthick slab showed that the cause was the presence of coarse particles of niobium carbonitride as constituent of the quasi eutectic Fe-Nb(C, N) that form because of the centerline segregation of niobium