[ES] Se establece la soldabilidad de funciones dúctiles de grafito según las características mecánicas alcanzadas, utilizando
un electrodo puro de Ni mientras se compara con uno más económico de Ni-Fe. Diferentes tratamientos térmicos
son propuestos y analizados. El electrodo de Ni puro mostró difusión de grafito desde el material original al cordón de
soldadura, dando como resultado una fase homogénea que mejoró la soldabilidad y redujo la fragilidad. Un pre tratamiento
a 350 °C y un recocido a 850 °C incrementaron la ductilidad y mejoró la soldabilidad.[EN] Weldability of spheroidal graphite ductile cast iron was established using a cheap Ni-Fe and a high purity Ni
electrode. A preheating treatment at 350 °C and an annealing treatment at 850 °C were carried out to improve
mechanical properties of welded pieces. The pure Ni electrode showed graphite diffusion in the bead with a
uniform distribution of phases, improving weldability and decreasing fragility. Preheating and annealing
treatments increased ductility and improved weldability.Pascual Guillamón, M.; Ferrer Giménez, C.; Rayón Encinas, E. (2009). Weldability of spheroidal graphite ductile cast iron using Ni / Ni-Fe electrodes. Revista de Metalurgia. 45(5):334-338. doi:10.3989/revmetalm.0814S33433845

C. Ferrer

Cembrero

E. Rayón

M. Pascual

English

Crossref

Weldability of spheroidal graphite ductile cast iron using Ni / Ni-Fe electrodes

[ES] Se establece la soldabilidad de funciones dúctiles de grafito según las características mecánicas alcanzadas, utilizando
un electrodo puro de Ni mientras se compara con uno más económico de Ni-Fe. Diferentes tratamientos térmicos
son propuestos y analizados. El electrodo de Ni puro mostró difusión de grafito desde el material original al cordón de
soldadura, dando como resultado una fase homogénea que mejoró la soldabilidad y redujo la fragilidad. Un pre tratamiento
a 350 °C y un recocido a 850 °C incrementaron la ductilidad y mejoró la soldabilidad.[EN] Weldability of spheroidal graphite ductile cast iron was established using a cheap Ni-Fe and a high purity Ni
electrode. A preheating treatment at 350 °C and an annealing treatment at 850 °C were carried out to improve
mechanical properties of welded pieces. The pure Ni electrode showed graphite diffusion in the bead with a
uniform distribution of phases, improving weldability and decreasing fragility. Preheating and annealing
treatments increased ductility and improved weldability.Pascual Guillamón, M.; Ferrer Giménez, C.; Rayón Encinas, E. (2009). Weldability of spheroidal graphite ductile cast iron using Ni / Ni-Fe electrodes. Revista de Metalurgia. 45(5):334-338. doi:10.3989/revmetalm.081433433845

Pascual Guillamón, Manuel

Ferrer Giménez, Carlos

Rayón Encinas, Emilio

RiuNet

rEVISTa dE METalUrGIa, 45 (5)SEPTIEMBrE-OCTUBrE, 334-338, 2009ISSn: 0034-8570eISSn: 1988-4222doi: 10.3989/revmetalm.0814334Weldability of spheroidal graphite ductile cast iron using Ni / Ni-Fe electrodes(•)M. Pascual*, C. Ferrer* y E. Rayón*Abstract Weldability of spheroidal graphite ductile cast iron was established using a cheap Ni-Fe and a high purity Nielectrode. A preheating treatment at 350 °C and an annealing treatment at 850 °C were carried out to improvemechanical properties of welded pieces. The pure Ni electrode showed graphite diffusion in the bead with auniform distribution of phases, improving weldability and decreasing fragility. Preheating and annealingtreatments increased ductility and improved weldability.Keywords Weldability; Ductile iron; Electrodes; Microstructures; Arc welding.Soldabilidad de aleaciones dúctiles de grafito esferoidal utilizandoelectrodos de Ni y Ni-FeResumen Se establece la soldabilidad de funciones dúctiles de grafito según las características mecánicas alcanzadas, utilizan-do un electrodo puro de Ni mientras se compara con uno más económico de Ni-Fe. Diferentes tratamientos térmicosson propuestos y analizados. El electrodo de Ni puro mostró difusión de grafito desde el material original al cordón desoldadura, dando como resultado una fase homogénea que mejoró la soldabilidad y redujo la fragilidad. Un pre trata-miento a 350 °C y un recocido a 850 °C incrementaron la ductilidad y mejoró la soldabilidad.Palabras clave Soldadura; Electrodos; Microestructuras; Soldadura por arco.1.  INTRODUCTIONIn fabrication industries, there exists high interestto establish a welding procedure for ductile castiron as this material has high mechanical propertiesas well as low cost. Studies were reported earlierabout the influence of thermal treatments andwelding techniques on the weldability of ductileiron using Ni electrodes [1 and 2]. Studies on mechanicalproperties of ductile cast iron welded by means ofoxyacetylene and arc welding techniques usingeither nickel or gray cast iron electrodes showedthat mechanical properties of the weld metal weldedwith gray iron electrodes were inferior than thatwelded with Ni electrodes[3]. As nickel can dissolvegraphite present in ductile iron (parent material)germinating as spherulites with a lower average sizefragile carbides and martensite structures are notformed facilitating uniform compositions in theweldment providing a high ductility and a lowfragility.The aim of the present work is to establish awelding procedure for spheroidal graphite ductilecast iron and compare the weld quality obtainedusing a low priced Fe-Ni electrode with that obtainedusing a pure Ni electrode. The weldability is evaluatedfrom the mechanical properties and microstructuresof weldments.2.  EXPERIMENTAL PROCEDUREDuctile cast iron samples of size 300 mm × 95 mm ×6 mm were obtained by casting in a sand mould. Themicrostructure of the samples was found to consist offerritic-pearlitic matrix containing uniform distribution(•) Trabajo recibido el día 22 de abril de 2008 y aceptado en su forma final el día 12 de marzo de 2009.* Instituto de Tecnología de Materiales, Universidad Politécnica de Valencia, Camí de Vera s/n. E-46022, Valencia, Spain. Pascual Guillamón,Manuel, +34 9638776245, mpascual@mcm.upv.es.WEldaBIlITy OF SPhErOIdal GraPhITE dUCTIlE CaST IrOn USInG nI / nI-FE ElECTrOdESSOldaBIlIdad dE alEaCIOnES dúCTIlES dE GraFITO ESFErOIdal UTIlIzandO ElECTrOdOS dE nI y nI-FErEV. METal. MadrId, 45 (5), SEPTIEMBrE-OCTUBrE, 334-338, 2009, ISSn: 0034-8570, eISSn: 1988-4222, doi: 10.3989/revmetalm.0814 335of graphite spherulites. Its chemical composition wasobtained using dispersive X-ray technique as: C, 3.83%, Mn, 0.15 %, Ni, 0.01 %, Cu, 0.03 %, Si, 2.62 %,P, 0.03 %, Cr, 0.04 %, Mo, 0.01 %, Mg, 0.04 % andits mechanical properties are given in table I.Manual metal arc welding was employed to jointhe ductile cast iron plates. The welding current of140 A, a.c., with a root gap of 1.5 mm was used inorder to obtain a good weld penetration. Two electrodehaving compositions of 57.2 % Ni + 41 % Fe (otherelements were 0.66 % C, 0.16 % Si, 0.85 % Mn)and 97.6 % Ni (0.30 % C, 0.20 %Si, 0.005 % P,0.005 % S, 0.2 % Mn and 1 % Fe) were used. Figure1 shows the joint design (Fig. 1 a) and electrodeangle of 70° with respect to the top surface of theplates (Fig. 1 b)). The welding speed used for theunpreheated and preheated pieces with a 57.2 % Nielectrode was 16.8 cm·min–1 and 22.8 cm·min–1respectively, and the speed for the 97.6 % Ni was19.2 cm·min–1 and 15.6 cm·min–1 respectively.In order to establish the effects of preheatingand annealing treatments, three types of weldingwere performed. In the first case the plates to bejoined were preheated at 350 °C and joined. In thesecond case, the plates were joined withoutpreheating and postheating. In the third case, theplates joined without preheating were annealed at850 °C for one hour.Samples were prepared from all as-welded andtreated plates by cutting it at its centres and polishedTable I. Mechanical properties of the parent metal and weld jointTabla I. Propiedades mecánicas del material original y del metal soldadoType of Electrode Ultimate Yield %  Vickers hardness of Place oftreatment used strength limit Elon- weld joint failure(MPa) (MPa) gation MR Bead HAZno preheating Fe-ni 520 460 8 618 210 360 Mrni 97.6 % 400 360 11 480 180 330 Mr350° C preheating Fe-ni 480 410 12 330 180 240 Mrni 97.6 % 340 335 14 300 175 230 Bead region850° C annealing Fe-ni 400 379 14 321 185 180 Bead regionni 97.6 % 388 342 16 251 170 178 Bead regionParent material — 470 330 6 — — 230 —Figure 1. Joint design and position of electrode. (a) Joint design. (b) Electrode’s angle and bead’sscheme viewed from the front of the bead.Figura 1. Esquema de soldadura y posición del electrodo. (a) Esquema de dos piezas visto desdeel frente. (b) Esquema del ángulo del electrodo y cordón de soldadura mostrado desde el avance dela soldadura.M. PaSCUal, C. FErrEr y E. rayón336 rEV. METal. MadrId, 45 (5), SEPTIEMBrE-OCTUBrE, 334-338, 2009, ISSn: 0034-8570, eISSn: 1988-4222, doi: 10.3989/revmetalm.0814as well as etched using standard metallurgicalprocedure. Photomicrographs were taken to analysethe microstructures at various zones. VickersMicrohardness values were obtained on threedistinguished regions such as weld metal, fusionzone or melt region (MR) and heat affected zone(HAZ) using a Matsuzawa machine (model MHT2)under a load of 300 N. Yield and ultimate tensilestrengths of all welded plates were evaluated by aInstron tensile machine (model 4204) at a constantcrosshead speed of 1 mm/min. Both hardness andstrength values obtained are presented in table I.3. RESULTSThe influence of thermal treatments on weldabilityof ductile iron and comparison of weld qualityobtained using a low priced Fe-Ni electrode withthat obtained using a pure Ni electrode were carriedout in order to improve the mechanical propertiesof welded joints. Those thermal treatments wouldresult in: (I) relieving residual stress, (II) diminishingthe cooling rate and (III) increasing the fluidityand diffusion of the molten material.3.1.  Ni and Fe-Ni electrode resultsFigure 2 a) shows a photomicrograph of the as-welded weld joint obtained with a 57.2 % Nielectrode without preheating and cooled in air.Three regions are shown clearly in the figure.The HAZ is observed to be a nodular ferriticpearlitic structure (dark matrix) very similar tothe parent metal structure. The dispersed darkflakes correspond to graphite concentrations andhad hardness of 360 HV. The hardness of the parentmetal is found to be 300 HV. The MR containsan acicular structure or needle like structure havingFigure 2. Optical photomicrographs of the weld joint welded and treated at different conditions: (a)as-welded with 57.2 % ni-Fe electrode, (b) as-welded with 97.6 % ni electrode, (c) preheated andas-welded with 57.2 % ni-Fe electrode (d) welded with 97.6 % ni electrode and annealed.Figura 2. Imagen de microestructuras de la pieza soldada con un (a) electrodo de 57,2 % Ni-Fe y sintratamiento térmico, (b) electrodo del 97,6 % Ni sin tratamiento térmico, (c) electrodo de 57,2 % Ni-Fecon precalentamiento de la pieza a 350 ºC, (d) electrodo 97,6 % Ni y posterior recocido a 850 ºC du-rante 1 h.WEldaBIlITy OF SPhErOIdal GraPhITE dUCTIlE CaST IrOn USInG nI / nI-FE ElECTrOdESSOldaBIlIdad dE alEaCIOnES dúCTIlES dE GraFITO ESFErOIdal UTIlIzandO ElECTrOdOS dE nI y nI-FErEV. METal. MadrId, 45 (5), SEPTIEMBrE-OCTUBrE, 334-338, 2009, ISSn: 0034-8570, eISSn: 1988-4222, doi: 10.3989/revmetalm.0814 337hardness of 618 HV (268 % higher than that ofthe parent material). It also has some smallergraphite flakes. From the tensile test, cracks wereobserved in MR which could be due to its higherfragile character. It is clear from the figure thatweld metal contains a brilliant matrix of nickelcontaining smaller graphite spherulites comparedwith that in the parent metal and has hardnessvalue of 210 HV.Figure 2 b) shows a typical microstructure ofthe weld joint welded with a 97.6 % Ni electrodewithout preheating. From the figure it is foundthat the HAZ is visually darker due to less amountof ferritic matrix structure resulting from thedissolution of ferrite in nickel. The hardness ofHAZ was found to be 330 HV (143 % higher thanthat of parent metal) and was very close to thehardness value of HAZ obtained using Fe-Nielectrodes. From the figure it is found that theMR contains several long needles acicular structures(ferritic-pearlitic structures) combined with somesmall needle acicular structures (martensite). Itwas found that the amount of martensite presentwas lesser than that was present in MR of previousweld joint obtained using Fe-Ni electrode whichwas also confirmed with its corresponding hardnessvalue of 480 HV. From the figure it is found thatthe weld bead contains ferritic-pearlitic structurewith a high concentration of small graphite flakesdistributed uniformly in the matrix resulting dueto the dissolution of graphite in nickel. Fromtable I it is found that the weld metal hardnessvalue is less. Though the bead had higher ductilitydue to the uniform distribution of graphite flakesfragile fracture cracks were observed in the MRwhich would be due to the higher hardness valueof martensite present.3.2.  Effects of preheatingFrom table I it is evident that when thermaltreatments were performed, the elongation isincreased and hardness is decreased in all regionsirrespective of the type of electrode used. Figure 2 c) shows a photomicrograph of theweld bead obtained with 57.2 % Ni electrode atpreheated condition. The brilliant metallic matrixobserved in the HAZ and in the parent material,indicates the dissolution of graphite in nickel.An open pearlitic structure inside an austeniticmatrix grew in that region. Nevertheless, graphitein the HAZ was disolved and small dots wereobserved instead of flake structures. The width ofthe MR is also decreased due to nickel contributionand its structure is found to be a pearlitic structurein the austenitic matrix. A laminar structure wasobserved at higher magnification. The (weld metal)bead region has smaller spheroidal graphite thanthat of parent material. Hardness obtained in theHAZ was 249 HV, very similar to the hardnessvalue of the parent material. The ductility wasincreased twice and the rest of values were verysimilar. The mode of failure observed from tensiletest was found to be ductile in the bead.Nevertheless, differences in the welded pieceobtained with a 97.6 % Ni electrode were observed.Figure 2 d) shows the typical microstructure of awelded cast iron using a 97.6 % Ni electrode atpreheated condition. It is observed that theconcentration of pearlitic structure in MR isdecreased. Graphite in form of smaller spherolytesgrew in the bead region and got distributeduniformly. This decreasing of the pearlitic structureconcentration and the smaller spherolyte formsmay be due to nickel metal, which absorbs carbon[4],dissolving it in its metallic matrix[5 and 6]. Fromtable I it is found that the ductility is increased to14 % and hardness diminished. It is also foundthat the yield limit is not affected significantly.3.3.  Annealing treatment resultsPost weld annealing of welded pieces was carriedout to reduce the concentration of hard phases,forcing them to form other structures such as lesshard ferritics or pearlitics. Figure 3 shows a typicalphotomicrograph of the welded piece joined witha 57.2 % Ni and 97.6 % Ni electrode at annealedcondition. It is found that the MR is not clearlyvisible in the piece welded with the 97.6 % Nielectrode, having very small width which mayprobably be due to the martensite transformationand also due to the dissolution of nickel into allzones. The spherulite graphite in the HAZ wasfound to be transformed into a ferritic phase. Inthe bead, graphite flakes are found to be smallerin size and distributed uniformly which is verysimilar to the structure that is obtained when aFe-Ni electrode is used except the presence ofsome amount of martensite. For both electrodesused, failures were found to be ductile and itoccurred always at the bead region (not in theMR as in previous cases). Mechanical propertiesof weld metal were similar to the parent metal.Ductility was found to be higher than that ofpreheated welded pieces.Figure 3 shows a photomicrograph of the weldedpiece with a 97.6 % nickel electrode and anM. PaSCUal, C. FErrEr y E. rayón338 rEV. METal. MadrId, 45 (5), SEPTIEMBrE-OCTUBrE, 334-338, 2009, ISSn: 0034-8570, eISSn: 1988-4222, doi: 10.3989/revmetalm.0814annealing treatment at 850 °C. The MR was notvisible probably due to the martensite transformationand also due to nickel dissolved into all zones.The spherulite graphite in the HAZ wastransformed into a ferritic phase. Graphite flakesgrew in the bead smaller in size and distributeduniformly. A very similar structure was obtainedwhen a Fe-Ni electrode was used (in this casesome amount of martensite grew). For bothelectrodes used, fractures were ductile and werealways found in the bead region (not in the MRas in previous cases). Mechanical properties weresimilar to the ones in the parent material.Elongation resulted from stress experiments washigher than results obtained from the weldedpieces with preheating.It is clear from the results that pure Ni electrodesare better than Fe-Ni electrodes to weld ductilecast iron due to the fact that a high nickelconcentration improves the graphite dissolution.In a Fe-C diagram at 3.8 % C the enhanceddissolution is found to be due to the ability ofnickel to self-dissolve into the austenite. Thus,when the liquid phase of the MR cools, nickelretains the austenite, preventing formation ofhard cementite. Furthermore, the carbon, insteadof forming cementite, grows as a nodular graphitestructure very similar to that of the parent material,as a result of the uniform growth of microstructuresin the three regions. The absence of hard structuresand the uniform composition provide it withenhanced ductility.4. CONCLUSIONSDuctile iron plates were welded using two differentelectrodes at three different conditions and itseffects were analyzed. The following conclusionswere arrived at:— High purity Ni electrodes showed a betterweldability than Ni-Fe electrodes resultingfrom enhanced ductility due to lower acicularstructures formed and better uniform distributionof graphite in the bead.— The preheating treatment increases the ductilityof the welded piece through minimizing hardand fragile microstructures.— An annealing treatment can be substituted forthe preheating treatment which also improvesthe ductility.REFERENCES[1] E.M- El-Banna, M.S. Nageda and M.M. Aboel Saadat, Mater. Lett. 42 (2000) 311-320.[2] E.M. El-Banna, Mater. Lett. 41 (1999) 20-26.[3] M. Pascual, J. Cembrero and F. Salas. Mater.Lett. 62 (2008) 1359-1362. [4] V.E. Buchanan, P.H. Shipway and D.G,Cartney, Wear 263 (2007) 99-110. [5] S. Kolukisa, J. Mater. Proces.Technol. 186(2007) 33-36.[6] J. Cembrero and M.Pascual, Rev. Metal. Madrid35 (1999) 392-401.Figure 3. Optical photomicrograph of the post weld annealed weld joint welded using (a) a 57.2 % nielectrode and (b) a 97.6 % ni electrode. Figura 3. Imagen de la microestructura de la soldadura realizada con (a) un electrodo del 57,2 % Niy (b) un electrodo del 97,6 % Ni. En ambas piezas se realizó un recocido a 850 ºC.

http://doaj.org/search?source=%7B%22query%22%3A%7B%22bool%22%3A%7B%22must%22%3A%5B%7B%22term%22%3A%7B%22id%22%3A%2278bb2ab9233940798b704fcbaea351c3%22%7D%7D%5D%7D%7D%7D

Weldability of spheroidal graphite ductile cast iron using Ni / Ni-Fe electrodes

Abstract

Similar works

Full text

Available Versions

Crossref

RiuNet