A new tungsten bronze ceramic oxide, Pb2-xK1+xLixNb5O15 (PKLN) (x =0.15) was prepared by high temperature solid-state reaction route. Structural and electrical properties are investigated using X-ray diffraction and dielectric measurements. Room temperature XRD pattern confirms the formation of the compound with an orthorhombic crystal system. The dielectric permittivity and the loss tangent of the sample have been measured in a frequency range 1Hz–1MHz and a temperature range 35–550 °C. Studies of dielectric properties show that the compound exhibits an anomaly at 425°C (usually called transition temperature).The electrical parameters of the material were studied using complex impedance spectroscopy showing that the compound exhibits non-Debye of relaxation process. In the paraelectric phase, activation energy was determined and the value is Eτ = 0.68 eV. The present ceramic is promising candidate for high dielectric constant and low loss dielectric ceramic.A new tungsten bronze ceramic oxide, Pb2-xK1+xLixNb5O15 (PKLN) (x =0.15) was prepared by high temperature solid-state reaction route. Structural and electrical properties are investigated using X-ray diffraction and dielectric measurements. Room temperature XRD pattern confirms the formation of the compound with an orthorhombic crystal system. The dielectric permittivity and the loss tangent of the sample have been measured in a frequency range 1Hz–1MHz and a temperature range 35–550 °C. Studies of dielectric properties show that the compound exhibits an anomaly at 425°C (usually called transition temperature).The electrical parameters of the material were studied using complex impedance spectroscopy showing that the compound exhibits non-Debye of relaxation process. In the paraelectric phase, activation energy was determined and the value is Eτ = 0.68 eV. The present ceramic is promising candidate for high dielectric constant and low loss dielectric ceramic