CORE
🇺🇦
make metadata, not war
Services
Services overview
Explore all CORE services
Access to raw data
API
Dataset
FastSync
Content discovery
Recommender
Discovery
OAI identifiers
OAI Resolver
Managing content
Dashboard
Bespoke contracts
Consultancy services
Support us
Support us
Membership
Sponsorship
Community governance
Advisory Board
Board of supporters
Research network
About
About us
Our mission
Team
Blog
FAQs
Contact us
Role of Clay Minerals Content and Calcite in Alkali Activation of Low-Grade Multimineral Clays
Authors
Bikmukhametov A.R.
Eskin A.A.
+5 more
Gubaidullina A.M.
Lygina T.Z.
Morozov V.P.
Rakhimov R.Z.
Rakhimova N.R.
Publication date
1 January 2020
Publisher
Abstract
© 2020 American Society of Civil Engineers. The increased contribution of science-intensive clean materials and technologies to the total industrial production is one of the essential prerequisites for the future of sustainable industrial development. Chemical activation based on a nonfired or low-temperature approach for the production of cementitious materials from glassy aluminosilicates, including calcined clays, is an intensively developing and promising clean technology. This study investigated the potential of calcined clays as precursors of alkali-activated cements (AACs) by considering three types of low-grade multimineral clays (with a clay mineral content of <20%). The alkali activation of the calcined clays was analyzed based on the type and content of clay minerals, presence of calcite, calcination temperature, type of alkali activator, and curing conditions. The results indicated that clays containing 20% of 21 layer lattice clay minerals are not suitable as precursors of AACs, while those containing 9%-12% of 11 and/or 21 layer lattice minerals combined with 29%-32% calcite lead to hardened pastes displaying compressive strengths of up to 12.4 MPa after 2 days and 20 MPa after 28 days and after steam curing. The reaction products of 6M NaOH-activated systems determined by XRD, TG/DSC, and FTIR spectroscopy analyses were X-ray amorphous binder gel, calcite (CaCO3), clinozoisite (Ca2Al3(SiO4)(Si2O7)(O,OH)), and gaylussite (CaNa2(CO3)(H2O)5)
Similar works
Full text
Available Versions
Kazan Federal University Digital Repository
See this paper in CORE
Go to the repository landing page
Download from data provider