In this research, researcher tested material of Asphalt Concrete (AC) with coarse aggregate from Lahat and fine aggregate from Tanjung Raja South Sumatera, asphalt from Pertamina with Pen. 60/70, while the filler material to be used is from Cement Baturaja. Proportion of filler to be used are 0%; 1,0%; 2,5%; and 4,0%. Marshall test results for each proportion of filler 0%, 1,0%, 2,5%, and 4,0% to the value of the KAO obtained 6,00%, 6,40%, 6,50% and 6,60%. Stability values respectively: 1225,67 kg, 1168,73 kg, 1187,60 kg, 1299,63 kg. Rated flow: 4,67 mm, 4,64 mm, 4,61 mm, 4,52 mm. VIM values obtained: 4,411%, 5,146%, 3,076% and 2,953%. VMA values obtained: 16,778%, 18,240%, 16,682% and 16,769%. VFA values obtained: 73,716%, 71,789%, 81,563%, 82,394%. Marshall Quotient: 262,77 kg / mm, 251,99 kg / mm, 257,54 kg / mm, and 287,88 kg / mm. Stability rest: 87,00%, 85,86%, 87,19% and 88,43%. The test results showed that while all Asphalt concrete mix with cement filler additive proposition to meet the criteria specified loss of stability due to immersion for 7 days is greater than 75%. From all asphalt concrete mixture obtained show that using the proportion of filler cement additive increase by 4% in asphalt concrete mix will increase the stability of the mixture, with a long soaking in water for 3 days. With the addition of additive filter using the proportion of cement by 4% in the asphalt mixture will be obtained concrete pavement material that can withstand heavy traffic load, during the service life of the road.