In this work, it was performed a thermal liquefaction of a sub-bituminous coal from
La Yolanda colliery (Valle del Cauca) with low density polyethylene waste in presence of tetraline and hydrogen. Experimental conditions used were a batch reactor of 115 ml magnetically stirred, temperatures of 380, 400, 420C, mass relation coal/poliethylene/tetraline of 1/5/3 and residence time of 30 minutes. Results showed that for the thermal coliquefaction using tetraline, conversion decrease with increase of temperature, whereas oils, asphaltenes, preasphaltenes and selectivity have a contrary behavior. Results also showed that, at 400 C, both high conversion and asphaltenes concentration were obtained using coal and waste polyethylene only. However, at those conditions selectivity to oils was lower than 20%.En este trabajo, un carbón sub bituminoso de la mina La Yolanda (Valle del Cauca), se colicuó térmicamente con residuos de polietileno de baja densidad (LDPE), en presencia de tetralina e hidrógeno. Se usó un reactor batch de 115 ml y agitación magnética, temperaturas de 380, 400 y 420C, relaciones de masa carbón/polietileno/tetralina 1/5/3 y tiempo de residencia de 30 minutos. Los resultados muestran que para la colicuefacción térmica en presencia de
tetralina, la conversión total y la distribución de productos fueron una función de la temperatura de reacción; la conversión decrece mientras que los aceites, asfaltenos, preasfaltenos y la selectividad se incrementan con la temperatura. Los resultados también muestran que elevadas conversiones y concentración de asfaltenos fueron obtenidas a 400C utilizando una mezcla de carbón polietileno únicamente. En estas condiciones, la selectividad hacia aceites usualmente fue más baja que el 20%