CORE
🇺🇦
make metadata, not war
Services
Services overview
Explore all CORE services
Access to raw data
API
Dataset
FastSync
Content discovery
Recommender
Discovery
OAI identifiers
OAI Resolver
Managing content
Dashboard
Bespoke contracts
Consultancy services
Support us
Support us
Membership
Sponsorship
Community governance
Advisory Board
Board of supporters
Research network
About
About us
Our mission
Team
Blog
FAQs
Contact us
TiO2/SiO2复合薄膜的形成历程与超亲水性关系
Authors
蒋新
陈喜明
鲁波娜
Publication date
1 January 2004
Publisher
Abstract
考察了溶胶-凝胶法制备TiO2/SiO2复合薄膜过程中,正硅酸乙酯(TEOS)的水解时间与膜的超亲水性的关系,通过XRD分析了SiO2添加量对TiO2锐钛矿晶型的影响,并研究复合薄膜的表面处理对其亲水性的影响。实验发现,当无因次反应时间为0.4时,复合薄膜的亲水性最好;SiO2的引入能够抑制金红石晶型的生长,最佳含量在10~20%
Similar works
Full text
Available Versions
Institutional Repository of Institute of Process Engineering, CAS (IPE-IR)
See this paper in CORE
Go to the repository landing page
Download from data provider
oai:ir.ipe.ac.cn:122111/44149
Last time updated on 11/04/2021