Порівняльна високотемпературна зносостійкість сплаву ЧС88У-ВІ і стелліта Х30Н50Ю5Т2

Abstract

The optimal compositions and application techniques of wear-resistant alloys on platforms of turbine blades are discussed. It is demonstrated that the serious problems arise when choosing the necessary alloying materials despite the apparent variety of them. Such a choice is significantly complicated by the lack of quantitative characteristics of wear-resistance of widely used alloying materials and basic heat-resistant alloys. Consequently, the aim of the study was to determine the quantitative comparative characteristics of wear-resistance of the ЧС88У-ВИ casting heat-resistant nickel alloy and the Х30Н50Ю5Т2 stellite at peak temperatures of gas turbine engines exploitation in the conditions most closely resembling the actual ones. It is established that the ЧС88У-ВИ alloy in the conditions of high temperature tests (~ 1150 ºС) which are close to the solution temperatures of the γ′-phase demonstrates the considerably higher resistance than the Х30Н50Ю5Т2stellite.Показано, что при кажущемся обилии наплавочных материалов при их выборе возникают серьезные проблемы. В этой связи целью исследований явилось определение количественных сравнительных характеристик износостойкости литейного жаропрочного никелевого сплава ЧС88У-ВИ и стеллита Х30Н50Ю5Т2. Установлено, что стойкость сплава ЧС88У-ВИ при температурах испытаний, близких к температурам растворения γ′-фазы значительно выше, чем стеллита.Показано, що при уявній великій кількості наплавочних матеріалів при їх виборі виникають серйозні проблеми. У цьому зв'язку метою досліджень було визначення кількісних порівняльних характеристик зносостійкості ливарного жароміцного нікелевого сплаву ЧС88У-ВИ та стеліту Х30Н50Ю5Т2. Установлено, що стійкість сплаву ЧС88У-ВИ, при температурах випробувань, близьких до температури розчинення γ'-фази, значно вища, ніж стеліту