Abstract. This work summarizes recent data on minority carrier lifetime in n-and p-type double heterostructures (DHs) of 0.5-0.6 eV GaInAsSb confined with GaSb and AlGaAsSb cap layers. Recombination times were measured by time-resolved photoluminescence (TRPL) and by optical frequency response (OFR) to sinusoidal excitation. It was shown that one of the mechanisms responsible for interface recombination in GaSb/GaInAsSb/GaSb DHs is thermionic emission of carriers over the heterobarrier. Considerable improvement of carrier confinement was obtained with 1 eV AlGaAsSb cap layers. Optimization of the epitaxial growth resulted in a recombination velocity at GaInAsSb/AlGaAsSb interface as low as 30 cm/s