Doping and isolation of GaN, InGaN and InAlN using ion implantation
Both n- and p-type doping have been achieved in GaN using Si{sup +} or Mg{sup +}/P{sup +} implantation, respectively, followed annealing at {ge} 1050{degrees}C. Using proximity rapid thermal annealing (10sec) the GaN surface retains both smooth morphology and its original stoichiometry. Variable temperature Hall measurements reveal approximate energy levels of 62meV for the implanted Si and 171meV for the Mg, which are similar to their values in epitaxially grown GaN. Implant isolation of both n- and p-type GaN, and n-type In{sub 0.75}Al{sub 0.25}N with multiple energy inert species (e.g. N{sup +} or F{sup +}) produces high resistivity ({ge}10{sup 8}{omega}/{open_square}) after subsequent annealing in the range 600-700{degrees}C. Smaller increases in sheet resistance are observed for In{sub x}Ga{sup 1-x}N (x=0.33-0.75) under the same conditions due to the smaller energy bandgaps and the shallower energy levels of the damage-related states controlling the resistivity
Recommended from our members
High temperature surface degradation of III-V nitrides
The surface stoichiometry, surface morphology and electrical conductivity of AlN, GaN, InN, InGaN and InAlN was examined at rapid thermal annealing temperatures up to 1,150 C. The sheet resistance of the AlN dropped steadily with annealing, but the surface showed signs of roughening only above 1,000 C. Auger Electronic Spectroscopy (AES) analysis showed little change in the surface stoichiometry even at 1,150 C. GaN root mean square (RMS) surface roughness showed an overall improvement with annealing, but the surface became pitted at 1,000 C, at which point the sheet resistance also dropped by several orders of magnitude, and AES confirmed a loss of N from the surface. The InN surface had roughened considerably even at 650 C, and scanning electron microscopy (SEM) showed significant degradation. In contrast to the binary nitrides the sheet resistance of InAlN was found to increase by {approximately} 10{sup 2} from the as grown value after annealing at 800 C and then remain constant up to 1,000 C, while that of InGaN increased rapidly above 700 C. The RMS roughness increased above 800 C and 700 C respectively for InAlN and InGaN samples. In droplets began to form on the surface at 900 C for InAlN and at 800 C for InGaN, and then evaporate at 1,000 C leaving pits. AES analysis showed a decrease in the N concentration in the top 500 {angstrom} of the sample for annealing {ge} 800 C in both materials
High Temperature Surface Degradation of III-V Nitrides
The surface stoichiometry, surface morphology and electrical conductivity of AlN, GaN, InN, InGaN and InAlN was examined at rapid thermal annealing temperatures up to 1,150 C. The sheet resistance of the AlN dropped steadily with annealing, but the surface showed signs of roughening only above 1,000 C. Auger Electronic Spectroscopy (AES) analysis showed little change in the surface stoichiometry even at 1,150 C. GaN root mean square (RMS) surface roughness showed an overall improvement with annealing, but the surface became pitted at 1,000 C, at which point the sheet resistance also dropped by several orders of magnitude, and AES confirmed a loss of N from the surface. The InN surface had roughened considerably even at 650 C, and scanning electron microscopy (SEM) showed significant degradation. In contrast to the binary nitrides the sheet resistance of InAlN was found to increase by {approximately} 10{sup 2} from the as grown value after annealing at 800 C and then remain constant up to 1,000 C, while that of InGaN increased rapidly above 700 C. The RMS roughness increased above 800 C and 700 C respectively for InAlN and InGaN samples. In droplets began to form on the surface at 900 C for InAlN and at 800 C for InGaN, and then evaporate at 1,000 C leaving pits. AES analysis showed a decrease in the N concentration in the top 500 {angstrom} of the sample for annealing {ge} 800 C in both materials
Recommended from our members
Chlorine-based plasma etching of GaN
The wide band gap group-III nitride materials continue to generate interest in the semiconductor community with the fabrication of green, blue, and ultraviolet light emitting diodes (LEDs), blue lasers, and high temperature transistors. Realization of more advanced devices requires pattern transfer processes which are well controlled, smooth, highly anisotropic and have etch rates exceeding 0.5 {micro}m/min. The utilization of high-density chlorine-based plasmas including electron cyclotron resonance (ECR) and inductively coupled plasma (ICP) systems has resulted in improved GaN etch quality over more conventional reactive ion etch (RIE) systems
Molecular dynamics simulation of the early stages of the synthesis of periodic mesoporous silica
We present results of detailed atomistic modeling of the early stages of the synthesis of periodic mesoporous silica using molecular dynamics. Our simulations lead to the proposal of a mechanism that validates several previous experimental and modeling studies and answers many controversial issues regarding the synthesis of mesoporous silicas. In particular, we show that anionic silicates interact very strongly with cationic surfactants and, significantly adsorb on the surface of micelles, displacing a fraction of previously bound bromide counterions. This induces an increase in micelle size and also enhances silica condensation at the micelle surface. The presence of larger silica aggregates in solution further promotes the growth of micelles and, by binding to surfactant molecules in different micelles, their aggregation. This work demonstrates the crucial role played by silica in influencing, by way of a cooperative templating mechanism, the structure of the eventual liquid-crystal phase, which in turn determines the structure of the porous material
Thinking dispositions for teaching : enabling and supporting resilience in context
Preparing pre-teachers for an increasingly challenging teaching profession is a complex work and requires teacher educators to engage in the careful design of both programmes and professional learning opportunities. This chapter explores how an explicit focus on thinking dispositions that enable effective teaching are developed in a Master of Teaching (Secondary) programme. This programme, delivered on-site at a secondary school, included carefully constructed teaching opportunities to support development of thinking dispositions. Ways of thinking and the impact they have on feelings, actions and beliefs will be examined along with how the implementation of our thinking dispositions framework supports the development of resilience in challenging teaching and learning contexts
Ultrafast single photon emitting quantum photonic structures based on a nano-obelisk
A key issue in a single photon source is fast and efficient generation of a single photon flux with high light extraction efficiency. Significant progress toward high-efficiency single photon sources has been demonstrated by semiconductor quantum dots, especially using narrow bandgap materials. Meanwhile, there are many obstacles, which restrict the use of wide bandgap semiconductor quantum dots as practical single photon sources in ultraviolet-visible region, despite offering free space communication and miniaturized quantum information circuits. Here we demonstrate a single InGaN quantum dot embedded in an obelisk-shaped GaN nanostructure. The nano-obelisk plays an important role in eliminating dislocations, increasing light extraction, and minimizing a built-in electric field. Based on the nano-obelisks, we observed nonconventional narrow quantum dot emission and positive biexciton binding energy, which are signatures of negligible built-in field in single InGaN quantum dots. This results in efficient and ultrafast single photon generation in the violet color region
- …