APPROACHING CRYOGENIC GE PERFORMANCE WITH PELTIER COOLED CDTE
A new class of hand-held, portable spectrometers based on large area (lcm2) CdTe detectors of thickness up to 3mm has been demonstrated to produce energy resolution of between 0.3 and 0.5% FWHM at 662 keV. The system uses a charge loss correction circuit for improved efficiency, and detector temperature stabilization to ensure consistent operation of the detector during field measurements over a wide range of ambient temperature. The system can operate continuously for up to 8hrs on rechargeable batteries. The signal output from the charge loss corrector is compatible with most analog and digital spectroscopy amplifiers and multi channel analyzers. Using a detector measuring 11.2 by 9.1 by 2.13 mm3, we have recently been able to obtain the first wide-range plutonium gamma-ray isotopic analysis with other than a cryogenically cooled germanium spectrometer. The CdTe spectrometer is capable of measuring small plutonium reference samples in about one hour, covering the range from low to high burnup. The isotopic analysis software used to obtain these results was FRAM, Version 4 from LANL. The new spectrometer is expected to be useful for low-grade assay, as well as for some in-situ plutonium gamma-ray isotopics in lieu of cryogenically cooled Ge
Recommended from our members
Large area silicon drift detectors for x-rays -- New results
Large area silicon drift detectors, consisting of 8 mm and 12 mm diameter hexagons, were fabricated on 0.35 mm thick high resistivity n-type silicon. An external FET and a low-noise charge sensitive preamplifier were used for testing the prototype detectors. The detector performance was measured in the range 75 to 25 C using Peltier cooling, and from 0.125 to 6 {micro}s amplifier shaping time. Measured energy resolutions were 159 eV FWHM and 263 eV FWHM for the 0.5 cm{sup 2} and 1 cm{sup 2} detectors, respectively (at 5.9 keV, {minus}75 C, 6 {micro}s shaping time). The uniformity of the detector response over the entire active area (measured using 560 nm light) was < 0.5%