Application of Induction Heating for Brazing Parts of Solar Collectors

This paper reports on the application of induction heating for brazing parts of solar collectors made of Al alloys. The tube-flange joint is a part of the collecting pipe of a solar collector. The main task was to design an induction coil for this type of joint, and to select the optimum brazing parameters. Brazing was performed with AlSi12 brazing alloy, and corrosive and non-corrosive flux types were also applied. The optimum brazing parameters were determined on the basis of testing the fabricated brazed joints by visual inspection, by leakage tests, and by macro- and micro-analysis of the joint boundary. The following conditions can be considered to be the best for brazing Al materials: power 2.69 kW,brazing time 24 s, flux BrazeTec F32/80

The influence of heat treatment on properties of lead-free solders

The article is focused on the analysis of degradation of properties of two eutectic lead-free solders SnCu0.7 and SnAg3.5Cu0.7. The microstructures of the intermetallic compound (IMC) layers at the copper substrate - solder interface were examined before and after heat treatment at 150°C for 50, 200, 500 and 1000 hours. The thickness of IMC layers of the Cu6Sn5 phase was growing with the increasing time of annealing and shown the typical scallops. For the heat treatment times of 200 hours and longer, the Cu3Sn IMC layers located near the Cu substrate were also observed. The experiments showed there is a link between the thickness of IMC layers and decrease of the shear strength of solder joints. In general, the joints made of the ternary solder showed higher shear strength before and after heat treatment in comparison to joints from solder SnCu0.7

Application of Induction Heating for Brazing Parts of Solar Collectors

This paper reports on the application of induction heating for brazing parts of solar collectors made of Al alloys. The tube-flange joint is a part of the collecting pipe of a solar collector. The main task was to design an induction coil for this type of joint, and to select the optimum brazing parameters. Brazing was performed with AlSi12 brazing alloy, and corrosive and non-corrosive flux types were also applied. The optimum brazing parameters were determined on the basis of testing the fabricated brazed joints by visual inspection, by leakage tests, and by macro- and micro-analysis of the joint boundary. The following conditions can be considered to be the best for brazing Al materials: power 2.69 kW,brazing time 24 s, flux BrazeTec F32/80

The influence of heat treatment on properties of lead-free solders

The article is focused on the analysis of degradation of properties of two eutectic lead-free solders SnCu0.7 and SnAg3.5Cu0.7. The microstructures of the intermetallic compound (IMC) layers at the copper substrate - solder interface were examined before and after heat treatment at 150°C for 50, 200, 500 and 1000 hours. The thickness of IMC layers of the Cu6Sn5 phase was growing with the increasing time of annealing and shown the typical scallops. For the heat treatment times of 200 hours and longer, the Cu3Sn IMC layers located near the Cu substrate were also observed. The experiments showed there is a link between the thickness of IMC layers and decrease of the shear strength of solder joints. In general, the joints made of the ternary solder showed higher shear strength before and after heat treatment in comparison to joints from solder SnCu0.7