Effect of different evaporation periods on microtensile bond strength of an acetone-based adhesive to dentin
Objective: Solvent content of a contemporary dental adhesive affect the bonding process, especially in the case of acetone based adhesives. The aim of this study was to evaluate the effect of different air-drying periods on microtensile bond strength (MTBS) of a total-etch adhesive to dentin.
Materials and Methods: Prime & Bond NT (Dentsply-USA) was used with different air-drying periods (0, 2, 5, 10, 30sec) for bonding a composite resin to prepared dentin. The specimens were then subjected to a tensile force until fracture and the MTBSs of the samples were recorded. Failure modes of the fractured samples were also determined using stereomicroscope and scanning electron microscopy. Data were analyzed using ANOVA and Bonferroni tests (P = 0.05).
Results: With increasing the air-drying periods, the MTBSs were increased until the 5 second air-blowing; after that, with increasing the air-drying periods, the MTBSs decreased. Both, the most complicated failure and the strongest bond were seen in the 5 sec air-drying group. Conclusion: There is an optimum air-drying time for acetone based adhesives which results in the strongest bond to dentin
Effect of Curing Direction on Microtensile Bond Strength of Fifth and Sixth Generation Dental Adhesives
Background and Aims: Composite restorative materials and dental adhesives are usually cured with light sources. The light direction may influence the bond strength of dental adhesives. The aim of this study was to evaluate the effect of light direction on the microtensile bond strength of fifth and sixth generation dental adhesives.Materials and Methods: Prime & Bond NT and Clearfil SE bond were used with different light directions.Sixty human incisor teeth were divided into 4 groups (n=15). In groups A and C, Clearfil SE bond with light curing direction from buccal was used for bonding a composite resin to dentin. In groups B and D, Prime & Bond NT with light curing direction from composite was used. After thermocycling the specimens were subjected to tensile force until debonding occurred and values for microtensile bond strength were recorded. The data were analyzed using two-way ANOVA and Tukey post hoc test.Results: The findings showed that the bond strength of Clearfil SE bond was significantly higher than that of Prime&Bond NT (P<0.001). There was no significant difference between light curing directions (P=0.132).Conclusion: Light curing direction did not have significant effect on the bond strength. Sixth generation adhesives was more successful than fifth generation in terms of bond strength to dentin