Selection criteria of lustrous carbon carriers in the aspect of properties of greensand system

Carbonaceous additives have often been regarded as problem ones to solve and improve the surface finish of iron castings, but at the same time they cause other issues such as increased loss on ignition, total fines and moisture in greensand systems. With the correct selection of carbonaceous additive, the combination of low ash, high volatile and lustrous carbon content coupled with the key element grading size, ensures that produced castings are free from metal penetration and surface related problems

Neškodljivost kalupnih pjesaka sa bentonitom i svijetlećim nositeljima ugljika

Procedures have been developed to determine the volume, rate and composition (particularly BTEX: benzene, toluene, ethylbenzene and xylenes and PAHs (polycyclic aromatic hydrocarbons)) of gas evolution from moulds and cores prepared with various binders as a means of harmfulness of moulding sands. The rate of gas evolution from green sands with four different lustrous carbon carrier and BTEX content were determined. The gas evolution rates are highest in the range of about 20 to 30 s after contact with molten metal. In practice during the first 200-250 s the total emission of gases generated in investigated samples occurred. The main emitted component from the BTEX group was benzene.Postupci su razvijeni za određivanje volumena, brzine i sastava (posebice BTEX: benzen, toluen, etilbenzen, xilana) i PAH (policiklički automatski hidrokarbonati) plina koji nastaje iz kalupa i jezgri na različitim nosačima u težnji za neškodljivost kalupnih pijesaka. Brzine nastajanja plina iz pripravljenih pijesaka sa 4 različita svijetleća nositelja ugljika i sadržajem BTEX su određeni. Brzine nastajanja plina su najveće u razini 20 do 30 s poslije dodira sa rastopljenim metalom. Praktično, tijekom prvih 200-250 s ostvaruje se ukupna emisija stvorenih plinova u istraživanim uzorcima. Iz BTEX skupine, benzen je glavna emitirajuća komponenta

X-Ray Computed Tomography in the Nondestructive Testing of Ductile Iron Castings

W artykule przedstawiono aktualne możliwości urządzeń pomiarowych, jakimi są tomografy komputerowe (CT), zdolnych do wykonania pełnych prześwietleń odlewów o grubości ścianek przekraczającej 80 mm. Wszystkie badania nieniszczące (NDT) zostały wykonane na wybranych odlewach z żeliwa sferoidalnego i szarego wykonanych w Spółce Akcyjnej Odlewnie Polskie w Starachowicach. Przedstawiono zasadę działania i ogólną budowę tomografów komputerowych oraz możliwości ich wykorzystania. Dodatkowo pokazano możliwości CT przy wizualizacji wyników i zestawieniu ich z dokumentacją 3D. Przedstawiono perspektywy oraz ograniczenia przy wykrywaniu i określaniu wad w odlewach.Actual possibilities of the computer-aided X-ray tomography equipment (CT) were presented illustrated by examples of devices capable to analyze the 80 mm thickness castings. All presented results of the nondestructive tests are performed for iron castings produced by “Odlewnie Polskie” S.A. based in Starachowice. The base principles of operation and structure of CT scanners are shown as well as possibility of this devices. The possibilities of the CT are presented in the domains of the results visualization and of the comparison with 3D documentation. Prospects and limitation of the casting defects detection and identification are presented

Wykorzystanie spektrofotometrii do oznaczania zawartości montmorillonitu w masach formierskich z bentonitem

The theoretical bases of spectrophotometry used in analysis are discussed in the paper as well as the results of investigations of the montmorillonite content by means of the spectrophotometric adsorption of the Cu(II)-triethylenetetramine (Cu-TET) complex are presented. Bentonites originated from various producers (Sud Chemie, ZGM Zębiec S.A,) as well as samples of model moulding sands bonded by these bentonites were inwestigated in respect of their montmorillonite content. The montmorillonite content was measured in samples being at a room temperature and at temperatures of 400 °C and 700 °C. It was indicated, that the determined montmorillonite content in bentonite for the bentonites under investigation and for the model moulding sands with bentonites, are comparable, which proves that the quartz matrix, does not disrupt the measuring methodology and the applied spectrophotometric method is suitable for the moulding sands. It was found that at a temperature of 700 °C montmorillonite undergoes deactivation in the tested bentonites.W publikacji omówiono podstawy teoretyczne spektrofotometrii wykorzystywanej w analityce chemicznej oraz przedstawiono wyniki badań zawartości montmorillonitu metodą spektrofotometryczną adsorpcji kompleksu Cu(II)-trietylenotetraminy (Cu-TET). Zbadano bentonity pochodzące od różnych producentów (Sud-Chemie, ZGM Zębiec S.A.) oraz próbki modelowych mas formierskich wiązanych tymi bentonitami pod względem ich zawartości montmorillonitu. Zawartość montmorillonitu mierzono w próbkach w temperaturze pokojowej oraz w próbkach wygrzewanych w temperaturze 400 °C i 700 °C. Wykazano, że wyznaczone zawartości montmorillonitu w bentonicie dla rozpatrywanych bentonitów i mas modelowych z ich udziałem są porównywalne, co świadczy o tym, że osnowa kwarcowa, nie zakłóca metodyki pomiarowej, a stosowana metoda spektrofotometryczna nadaje się do wykorzystania w odniesieniu do mas formierskich. Stwierdzono, że w temperaturze 700 °C następuje dezaktywacja montmorillonitu w badanych bentonitach

Ocena szkodliwości żywic stosowanych jako nośniki węgla błyszczącego w masach z bentonitem

The assessment of harmfulness of two resins applied as a partial substitute of coal dust in moulding sands with bentonite - was performed in the paper. The emission value of compounds from the PAH and BTEX groups was assumed as the main harmfulness criterion. Also mixtures of the Kormix type prepared with additions of these resins were tested. Experiments were carried out in an argon atmosphere in a temperature range: 500-1300°. The obtained emission values of these substances were recalculated for 1% of lustrous carbon content in each carrier. It was assumed in the calculations, that the NW 1 and NW 2 carriers contain approximately 55% of lustrous carbon while the Kormix mixture approximately 15%. The critical temperature of forming compounds of the PAH group for the NW 1 carrier is 900°, while for the NW 2 carrier is 1100° (this is a temperature, at which the emission abruptly increases). In case of formation of compounds from the BTEX group the critical temperature for both lustrous carbon carriers is a temperature of 900°.W artykule dokonano oceny szkodliwości dwóch żywic stosowanych jako częściowy zamiennik pyłu węglowego w masach z bentonitem. Jako kryterium przyjęto wielkość emisji związków z grupy WWA oraz BTEX. Zbadano również mieszanki typu Kormix sporządzane z dodatkiem tych żywic. Badania przeprowadzono w atmosfer argonu w zakresie temperatury 500-1300°C. Uzyskane wartości wielkości emisji tych związków zostały przeliczone na 1% zawartości węgla błyszczącego w każdym z nośników . Do obliczeń np. przyjeęo, że nośniki NW 1 i NW 2 zawierają około 55% węgla błyszczącego, a mieszanki Kormix około 15%. Dla nośnika NW 1 temperatura krytyczna tworzenia się WWA jest 900°C, a dla nośnika NW 2 temperatura 1100°C (jest to temperatura, w której gwałtownie wzrasta emisja). W przypadku tworzenia się BTEX temperatura krytyczna, dla obu nosników węgla błyszczącego jest temperatura 900°C