4 research outputs found
Growth of abnormal planar faceted grains in nanocrystalline nickel containing impurity sulphur
Sodium/Na β″ Alumina Interface:Effect of Pressure on Voids
Three-electrode studies coupled with tomographic imaging of the Na/Na-β″-alumina interface reveal that voids form in the Na metal at the interface on stripping and they accumulate on cycling, leading to increasing interfacial current density, dendrite formation on plating, short circuit, and cell failure. The process occurs above a critical current for stripping (CCS) for a given stack pressure, which sets the upper limit on current density that avoids cell failure, in line with results for the Li/solid-electrolyte interface. The pressure required to avoid cell failure varies linearly with current density, indicating that Na creep rather than diffusion per se dominates Na transport to the interface and that significant pressures are required to prevent cell death, >9 MPa at 2.5</p
Modelling deformation and fracture of Gilsocarbon graphite subject to service environments
Commercial graphites are used for a wide range of applications. For example, Gilsocarbon graphite is used within the reactor core of advanced gas-cooled reactors (AGRs, UK) as a moderator. In service, the mechanical properties of the graphite are changed as a result of neutron irradiation induced defects and porosity arising from radiolytic oxidation. In this paper, we discuss measurements undertaken of mechanical properties at the micro-length-scale for virgin and irradiated graphite. These data provide the necessary inputs to an experimentally-informed model that predicts the deformation and fracture properties of Gilsocarbon graphite at the centimetre length-scale, which is commensurate with laboratory test specimen data. The model predictions provide an improved understanding of how the mechanical properties and fracture characteristics of this type of graphite change as a result of exposure to the reactor service environment.Materials and Environmen