Different Aspects of Cavitation Damages in Some Stainless Steels
Cavitation is an important factor in many areas of science and
engineering, including acoustics, chemistry and hydraulics. In this
paper the authors analyze the manner of cavitation damages in
different samples of stainless steels. Cavitation destruction was performed
in a magnetostrictive vibrating apparatus in Laboratory of Polytechnic
University of Timisoara, Romania. Cavitation erosion behaviour
was appreciated considering macrostructural analysis (both quantitative
and qualitative) made at stereomicroscope type OLYMPUS equipped
with QuickMicrophoto 2.2 software and structural analysis at scaning
electron microscope (SEM) at Philips SEM microscope. Finally conclusions
regarding specific structural features of cavitation at stainless
steels were revealed
Structural Analysis of Cavitation for Different Stainless Steels
The cavitation phenomenon is currently approaching all areas of technology
and modern industry, where are fluid in motion.
In this paper cavitational erosion was conducted on different samples
of stainless steels. The cavitation were performed in magnetostrictive
vibrating apparatus at Cavitation Laboratory (Polytechnic University of
Timisoara).
The present paper intends to identify specific structural features in
stainless steels. Several investigations were done: macrostructural
analysis (Olympus SZX57), scaning electron microscope (Philips SEM)
and X-ray diffraction (D8 ADVANCE). After quantitative and qualitative
investigations structural features were put in evidence on experimental
stainless steels
Correlation between Mechanical Properties—Structural Characteristics and Cavitation Resistance of Cast Aluminum Alloy Type 5083
The aluminum alloy type 5083, which has high corrosion resistance, excellent weldability, and good strength, is widely used in shipbuilding, automotive, aerospace, and industrial construction. The present paper has the aim of establishing a possible correlation between mechanical properties, structural characteristics, and cavitation erosion properties of the 5083 alloy after applying different heat treatments. Different homogenization heat treatments (350 °C, 450 °C) were applied, each followed by cooling in air and artificial aging at different temperature (140 °C and 180 °C) with three maintenance periods, 1 h, 12 h, and 24 h. The experiments concerning cavitation resistance of the experimental samples were completed in accordance with ASTM G32-2016. The cavitation erosion resistance were determined either by analytical diagrams MDER (or MDE) vs. cavity attack duration, or by measuring the maximum erosion attack by stereomicroscopy and scanning electron microscopy. Finally, the best combination of heat treatments applied to cast aluminum products type 5083 is homogenization at 350 °C followed by artificial aging at 180 °C, at which the highest mechanical characteristics are obtained, a resilience of 25 J/cm2, a grain size of 140–180 μm, and a maximum depth of the erosion MDEmax around 14–17 µm
Correlation between Mechanical Properties—Structural Characteristics and Cavitation Resistance of Cast Aluminum Alloy Type 5083
The aluminum alloy type 5083, which has high corrosion resistance, excellent weldability, and good strength, is widely used in shipbuilding, automotive, aerospace, and industrial construction. The present paper has the aim of establishing a possible correlation between mechanical properties, structural characteristics, and cavitation erosion properties of the 5083 alloy after applying different heat treatments. Different homogenization heat treatments (350 °C, 450 °C) were applied, each followed by cooling in air and artificial aging at different temperature (140 °C and 180 °C) with three maintenance periods, 1 h, 12 h, and 24 h. The experiments concerning cavitation resistance of the experimental samples were completed in accordance with ASTM G32-2016. The cavitation erosion resistance were determined either by analytical diagrams MDER (or MDE) vs. cavity attack duration, or by measuring the maximum erosion attack by stereomicroscopy and scanning electron microscopy. Finally, the best combination of heat treatments applied to cast aluminum products type 5083 is homogenization at 350 °C followed by artificial aging at 180 °C, at which the highest mechanical characteristics are obtained, a resilience of 25 J/cm2, a grain size of 140–180 μm, and a maximum depth of the erosion MDEmax around 14–17 µm