Effect of diffusion on coating microstructure and oxidation resistance of aluminizing steel

The effect of diffuse treatment on coating microstructure and oxidation resistance at high-temperature of hot-dip aluminum were studied by means of TEM, SEM and XRD. The results show that, the diffusion temperature has significant effect on structure of coatings and its oxidation resistance. After diffusion at 750 degreesC, the coating consists of thick outer surface layer (Fe2Al5+ FeAl2), thin internal layer (FeAl + stripe FeAl2), and its oxidation resistance is poor. After diffusion at 950 degreesC, the outer surface layer is composed of single FeAl2 phase, the internal layer is composed of FeAl phase, and its oxidation resistance declines due to the occurrence of early stage internal oxidation cracks in the coating. After diffusion at 850 degreesC, the outer surface layer becomes thinner and consists of FeAl2 Fe2Al5(small amount), the internal layer becomes thicker and consists of FeAl+spherical FeAl2, and the spheroidized FeAl2 phase in the internal layer and its existing in FeAl phase steadily improve the oxidation resistance of the coating

IMP质子治癌3D剂量探测系统

文章描述了中国科学院近代物理研究所(IMP)正在研制的IMP质子治癌装置3D剂量测量系统。该系统主要由2D剖面探测器、辐照深度和剂量探测器、射程调整器等组成。其中,多级双维位置灵敏平行板雪崩探测器(MPPAC)使用C3F8作为工作气体,工作气压为700Pa,阳极电压为+700V。对3组分α粒子测得位置分辨为0.54mm(FWHM)