Use of a zeolite synthesised from alkali treated kaolin as a K fertiliser: Glasshouse experiments on leaching and uptake of K by wheat plants in sandy soil

Zeolite N, a zeolite referred to in earlier publications as MesoLite, is made by caustic reaction of kaolin at temperatures between 80 °C and 95 °C. This material has a very high cation exchange capacity (CEC ≈ 500 meq/100 g). Soil column leaching experiments have shown that K-zeolite N additions greatly reduce leaching of NH4+ fertilisers but the agronomic effectiveness of the retained K+ and NH4+ is unknown. To measure the bioavailability of K in this zeolite, wheat was grown in a glasshouse with K-zeolite N as the K fertiliser in highly-leached and non-leached pots for four weeks and compared with a soluble K fertiliser (KCl). The plants grown in non-leached pots and fertilised with K-zeolite N were slightly larger than those grown with KCl. The elemental compositions in the plants were similar except for Si being significantly more concentrated in the plants supplied with K-zeolite N. Thus K-zeolite N may be an effective K-fertiliser. Plants grown in highly-leached pots were significantly smaller than those grown in non-leached pots. Plants grown in highly-leached pots were severely K deficient as half of the K from both KCl and K-zeolite N was leached from the pots within three days

K from zeolite: glasshouse trial for testing K availability to the plants

MesoLite, a zeolite material manufactured by NanoChem Holdings Pty Ltd is made by caustic reaction of kaolin at temperatures between 80-95°C. This material has a moderate surface area (9~12 m2/g) and very high cation exchange capacity (500meq/100g). To measure the availability of K in K-MesoLite to plants, wheat was grown with K-MesoLite or a soluble fertiliser (e.g. KCl) in non-leached pots in a glasshouse. The weights and elemental compositions of the plants were compared after four weeks growth. Plants grown with K-MesoLite were slightly larger than those grown with KCl. The elemental compositions of the plants were similar except for Si, which was significantly higher in the plants grown with K-MesoLite than in those fertilised with KCl. K from K-MesoLite is readily available to plants

Increasing the NH4+-retention efficiency of sandy soils by adding a modified kaolin material: MesoLite

Water and ammonium retention by sandy soils may be low and result in leaching of applied fertiliser. To increase water and nutrient retention, zeolite is sometimes applied as a soil ameliorant for high value land uses including turf and horticulture. We have used a new modified kaolin material (MesoLite) as a soil amendment to test the efficiency of NH4+ retention and compared the results with natural zeolite. MesoLite is made by caustic reaction of kaolin at temperature between 80-95°C; although it has a moderate surface area, its cation exchange capacity is very high;(SA=13m2/g,CEC=500meq/100g). A 13cm tall sand column filled with ~450g of sandy soil homogeneously mixed with 1, 2, 4, and 8g of MesoLite or natural zeolite per 1kg of soil was prepared. After saturation with local bore water, concentrated ammonium sulfate solution was injected at the base. Then, bore water was passed from bottom to top through the column at amounts up to 6 pore volumes and at a constant flow rate of 10ml/min using a peristaltic pump. Concentrations of leached NH4+ were determined using an AutoAnalyser. The concentration of NH4+ leached from the column with 0.4% MesoLite was greatly (90%) reduced relative to unamended soil. Under these conditions NH4+ retention by the soil-MesoLite mixture was 11.5 times more efficient than the equivalent soil-natural zeolite mixture. Glasshouse experiments conducted in a separate study show that NH4+ adsorbed by MesoLite is available to plants

Zeolite from alkali modified kaolin increases NH4+ retention by sandy soil: Column experiments

Sandy soils have low water and nutrient retention capabilities so that zeolite soil amendments are used for high value land uses including turf and horticulture to reduce leaching losses of NH4+ fertilisers. MesoLite is a zeolitic material made by caustic treatment of kaolin at 80-95oC. It has a moderately low surface area (9-12m2/g) and very high cation exchange capacity (494 cmol(+)/kg). Laboratory column experiments showed that an addition of 0.4% MesoLite to a sandy soil greatly (90%) reduced leaching of added NH4+ compared to an unamended soil and MesoLite is 11 times more efficient in retaining NH4+ than natural zeolite. Furthermore, NH4+-MesoLite slowly releases NH4+ to soil solution and is likely to be an effective slow release fertiliser