Shallow donor defect formation and its influence on semi-insulating indium phosphide after high temperature annealing with long duration

Fe-doped semi-insulating (SI) InP has become semi-conducting (SC) material completely after annealing at 900 V for 10 hours. Defects in the SC and SI InP materials have been studied by deep level transient spectroscopy (DLTS) and thermally stimulated current spectroscopy (TSC) respectively. The DLTS only detected Fe acceptor related deep level defect with significant concentration, suggesting the formation of a high concentration of shallow donor in the SC-InP TSC results confirmed the nonexistence of deep level defects in the annealed SI-InP. The results demonstrate a significant influence of the thermally induced defects on the electrical properties of SI-InP. The formation mechanism and the nature of the shallow donor defect have been discussed based on the results

Annealing and activation of silicon implanted in semi-insulating InP substrates

We have investigated the annealing and activation of silicon implanted in both as-grown Fe-doped semi-insulating (SI) InP substrate and undoped SI InP substrate obtained by annealing high purity conductive InP wafer (wafer-annealed). Si implantations were performed at an energy of 500 keV and a dose of 1 X 10(15) cm(-2). Following the implantations, rapid thermal annealing (RTA) cycles were carried out for 30 s at different temperatures. The results of Raman measurements show that for 700degreesC/30s RTA, the two Si-implanted SI InP substrates have acquired a high degree of lattice recovery and electrical activation. However, further Hall measurements indicate that the carrier concentration of the wafer-annealed SI InP substrate is about three times higher than that of the as-grown Fe-doped SI InP substrate. The difference can be ascribed to the low Fe concentration of the wafer-annealed SI InP substrate.These experimental data imply that the use of the wafer-annealed SI InP substrate can be conducive to the improvement of InP-based device performances. (C) 2003 Elsevier Ltd. All rights reserved

Fe-diffusion-induced defects in InP annealed in iron phosphide ambient

Photoluminescence (PL) and photo induced current transient spectroscopy (PICTS) have been used to study deep levels in semi-insulating (SI) InP prepared by annealing undoped InP in pure phosphorus (PP) and iron phosphide (IP) ambient. Defects are much fewer in IP SI-InP than in PP SI-InP. Deep-level-related PL emission could only be detected in IP SI-InP. The results indicate that Fe diffusion inhibits the thermal formation of a number of defects in annealed InP. A complex defect has been formed in the annealing process in the presence of Fe

Characterization of bulk ZnO single crystal grown by a CVT method - art. no. 68410F

Hall effect, photoluminescence spectroscopy (PL), mass spectroscopy and X-ray diffraction have been used to study bulk ZnO single crystal grown by a closed seeded chemical vapor transport method. Enhancement of n-type electrical conduction and increase of nitrogen concentration are observed of the ZnO samples after high temperature annealing. The results suggest that vacancy is dominant native defect in the ZnO material. These phenomena are explained by a generation of shallow donor defect and suppression of deep level defects in ZnO after the annealing

Annihilation of deep level defects in InP through high temperature annealing

Deep level transient spectroscopy (DLTS) and thermally stimulated current spectroscopy (TSC) have been used to investigate defects in semi-conducting and semi-insulating (SI) InP after high temperature annealing, respectively. The results indicate that the annealing in iron phosphide ambient has an obvious suppression effect of deep defects, when compared with the annealing in phosphorus ambient. A defect annihilation phenomenon has also been observed in Fe-doped SI-InP materials after annealing. Mechanism of defect formation and annihilation related to in-diffusion of iron and phosphorus is discussed. Nature of the thermally induced defects has been discussed based on the results. (c) 2007 Elsevier Ltd. All rights reserved

Native deep level defects in ZnO single crystal grown by CVT method - art. no. 68410I

Hall effect, photoluminescence (PL), infrared absorption, deep level transient spectroscopy (DLTS), and Raman scattering have been used to study property and defects of ZnO single crystal grown by a chemical vapor transport method (CVT). As-grown ZnO is N type with free electron density Of 10(16)-10(17)cm(-3). It has a slight increase after 900 degrees C annealing in oxygen ambient. The DLTS measurement revealed four deep level defects with energy at 0.30eV, 0.50eV, 0.68eV and 0.90eV in the as-grown ZnO sample, respectively. After the high temperature annealing, only the 0.5eV defect survive and has a concentration increase. PL results of the as-grown and annealed ZnO indicate that the well-known green emission disappear after the annealing. The result suggests a correlation between the 0.68eV defect and the green PL peak. Results of P-doped ZnO were also compared with the undoped ZnO sample. The nature of the defects and their influence on the material property have been discussed

Photoluminescence assessment of undoped semi-insulating InP wafers obtained by annealing in iron phosphide vapour

We have investigated the photoluminescence mapping characteristics of semi-insulating (SI) InP wafers obtained by annealing in iron phosphide ambience (FeP2-annealed). Compared with as-grown Fe-doped and undoped SI InP wafers prepared by annealing in pure phosphorus vapour (P-annealed), the FeP2-annealed ST InP wafer has been found to exhibit a better photoluminescence uniformity. Radial Hall measurements also show that there is a better resistivity uniformity on the FeP2-annealed Sl InP wafer. When comparing the distribution of deep levels between the annealed wafers measured by optical transient Current spectroscopy, we find that the incorporation of iron atoms into the Sl InP Suppresses the formation of a few defects. The correlation observed in this study implies that annealing in iron phosphorus ambience makes Fe atoms diffuse uniformly and occupy the indium site in the Sl InP lattice. As it stands, we believe that annealing undoped conductive InP in iron phosphide vapour is an effective means to obtain semi-insulating InP wafers with superior uniformity

Generation and suppression of deep level defects in InP

Deep level defects in as-grown and annealed n-type and semi-insulating InP have been studied. After annealing in phosphorus ambient, a large quantity of deep level defects were generated in both n-type and semi-insulating InP materials. In contrast, few deep level defects exist in InP after annealing in iron phosphide ambient. The generation of deep level defects has direct relation with in-diffusion of iron and phosphorus in the annealing process. The in-diffused phosphorus and iron atoms occupy indium sites in the lattice, resulting in the formation of P anti-site defects and iron deep acceptors, respectively. T e results indicate that iron atoms fully occupy indium sites and suppress the formation of indium vacancy and P anti-site, etc., whereas indium vacancies and P anti-site defects. are formed after annealing in phosphor-us ambient. The nature of the deep level defects in InP has been studied based on the results

Deep levels in semi-insulating InP obtained by annealing under iron phosphide ambiance

Deep levels in semi-insulating (SI) InP obtained by annealing in iron phosphide (IP) ambiance have been characterized by optical transient current spectroscopy (OTCS). Compared with the OTCS result of the SI InP prepared by annealing in pure phosphorus (PP) ambiance, the IP SI InP presents only two traps with activation energies of 0.20 and 0.63 eV, respectively. The results suggest that the diffusion of Fe-atoms suppresses the formation of a few defects in the IP SI InP. The nature of deep levels in the IP and PP SI InP has been discussed on the basis of these results. The relation between material property and defects in those SI InP has also been revealed. (C) 2002 American Institute of Physics