6 research outputs found
One-Pot Preparation of Metal–Polymer Nanocomposites in Irradiated Aqueous Solutions of 1-Vinyl-1,2,4-triazole and Silver Ions
Metal–polymer nanocomposite polyvinyltriazole–silver nanoparticles were obtained using one-pot synthesis in irradiated aqueous solutions of 1-vinyl-1,2,4-triazole (VT) and silver ions. Gel permeation chromatography data show that upon radiation initiation, the molecular weight of poly(1-vinyl-1,2,4-triazole) increases with increasing monomer concentration. To study the kinetics of polymerization and the features of the radiation–chemical formation of nanoparticles, UV-Vis spectroscopy was used. TEM images show a relatively small average size of the forming nanoparticles (2–3 nm) and a narrow size distribution, which shows the effective stabilization of nanoparticles by triazole substituents at a molar ratio of VT and silver ions of 25/1. The addition of ethyl alcohol was used to increase the efficiency of synthesis and suppress the crosslinking of macromolecules in solution. The results of the work show that aqueous–alcoholic solutions of 1 wt.% VT can be used to obtain soluble nanocomposite materials. 10 wt.% monomer solutions have prospects for use in the preparation of polymer gels filled with nanoparticles
Assembling of Metal-Polymer Nanocomposites in Irradiated Solutions of 1-Vinyl-1,2,4-triazole and Au(III) Ions: Features of Polymerization and Nanoparticles Formation
Gold nanoparticles (AuNPs) stabilized with poly(1-vinyl-1,2,4-triazole) (PVT) have been synthesized via a one-pot manner in irradiated solutions of 1-vinyl-1,2,4-triazole (VT) and Au(III) ions. The transmission electron microscopy examinations have shown that the sizes of nanoparticles formed range from 1 to 11 nm and are affected by the ratio of VT to gold ions. To study the kinetics peculiarities of the VT polymerization and assembling of AuNPs, UV-Vis spectroscopy was used. The analysis of the data obtained reveals that an inhibition period, influenced by Au(III) concentration, is followed by the polymerization of a monomer. Importantly, the absorbed doses, corresponding to the onset of rapid polymerization, correlate with the doses at which the accelerated formation of AuNPs begins. The kinetics aspects, which could lead to such an effect, are discussed
X-ray Induced Formation of Metal Nanoparticles from Interpolyelectrolyte Complexes with Copper and Silver Ions: The Radiation-Chemical Contrast
Radiation-induced preparation of metal nanostructures in coatings of interpolyelectrolyte complexes
Copper, silver and gold nanoparticles were obtained by reduction of metal ions under X-ray irradiation of “layer-by-layer” (LbL) coatings in a water-alcohol medium. The precursors for metal polymer composites (metallopolymer complexes) were prepared by sorption of metal ions in polyethyleneimine - poly (styrenesulfonic acid) and polyethyleneimine - poly (acrylic acid) coatings deposited on cotton fibers. EPR spectroscopy was use to characterize the complexation of metal ions in coatings with different chemical structure and variable number of polyanion-polycation layers. The effect of coating structure and thickness on the size and stability of nanoparticles was studied using TEM and microdiffraction measurements. Antibacterial activity was found for composites containing silver nanoparticles.The reported study was funded by RFBR according to the research project № 18-33-01155
Efficient size control of copper nanoparticles generated in irradiated aqueous solutions of star-shaped polyelectrolyte containers
Preparation of Biocidal Nanocomposites in X-ray Irradiated Interpolyelectolyte Complexes of Polyacrylic Acid and Polyethylenimine with Ag-Ions
Due to the presence of cationic units interpolyelectrolyte complexes (IPECs) can be used as a universal basis for preparation of biocidal coatings on different surfaces. Metallopolymer nanocomposites were successfully synthesized in irradiated solutions of polyacrylic acid (PAA) and polyethylenimine (PEI), and dispersions of non-stoichiometric IPECs of PAA–PEI containing silver ions. The data from turbidimetric titration and dynamic light scattering showed that pH 6 is the optimal value for obtaining IPECs. Metal polymer complexes based on IPEC with a PAA/PEI ratio equal to 3/1 and 1/3 were selected for synthesis of nanocomposites due to their aggregative stability. Studies using methods of UV–VIS spectroscopy and TEM have demonstrated that the size and spatial organization of silver nanoparticles depend on the composition of polymer systems. The average sizes of nanoparticles are 5 nm and 20 nm for complexes with a molar ratio of PAA/PEI units equal to 3/1 and 1/3, respectively. The synthesized nanocomposites were applied to the glass surface and exhibited high antibacterial activity against both gram-positive (Staphylococcus aureus) and gram-negative bacteria (Salmonella). It is shown that IPEC-Ag coatings demonstrate significantly more pronounced biocidal activity not only in comparison with macromolecular complexes of PAA–PEI, but also coatings of PEI and PEI based nanocomposites