Development of delamination in cross-ply laminates: effect of microstructure

Various aspects of the effect of microstructural randomness exhibited by carbon fibre-reinforced cross-ply laminates on the delamination damage mechanism is investigated in this paper. In the first part, the matrix cracks with different spacings measured in experiments are simulated using finite elements in order to obtain the levels of degradation and effective properties for a composite beam loaded in bending. The results show significant levels of degradation of obtained effective properties depicting the importance of accounting for the inherent stochasticity in these laminates. In the second part of the paper, initiation of delamination at an interface between 0° and 90° layers due to stress concentrations at tips matrix cracks is simulated for a beam under tension. Stochastic cohesive zone elements with fracture parameters presented as random fields are used to model this interface in a composite. Different values of the axial stress are obtained for initiation of damage for a number of realisations based on this approach. The results emphasize the need to take into consideration the microstructural randomness in fibre-reinforced laminates for adequate predictions of damage and load carrying capacities

Simulations of delamination in CFRP laminates: effect of microstructural randomness

Due to their high specific strength and stiffness, fibre-reinforced composite materials are being increasingly used in structural applications where a high level of performance is important (e.g. aerospace, automotive, offshore structures, etc.). Performance in service of these composites is affected by multi-mechanism damage evolution under loading and environmental conditions. For instance, carbon fibre-reinforced laminates demonstrate a wide spectrum of failure mechanisms such as matrix cracking and delamination. These damage mechanisms can result in significant deterioration of the residual stiffness and load-bearing capacity of composite components and should be thoroughly investigated. The delamination failure mechanism is studied in this paper for a double cantilever beam (DCB) loaded in Mode I. Several sensitivity studies are performed to analyse the effects of mesh density and of parameters of the cohesive law on the character of damage propagation in laminates. The microstructural randomness of laminates that is responsible for non-uniform distributions of stresses in them even under uniform loading conditions is accounted for in the model. The random properties are introduced with the use of Weibull’s two-parameter probability density function. Several statistical realisations are carried out which show that the effect of microstructure could significantly affect the macroscopic response emphasizing the need to account for microstructural randomness for accurate predictions of load-carrying capacity of laminate composite structures

Three-dimensional analysis of the effect of material randomness on the damage behaviour of CFRP laminates with stochastic cohesive-zone elements

Laminated carbon fibre-reinforced polymer (CFRP) composites are already well established in structural applications where high specific strength and stiffness are required. Damage in these laminates is usually localised and may involve numerous mechanisms, such as matrix cracking, laminate delamination, fibre de-bonding or fibre breakage. Microstructures in CFRPs are non-uniform and irregular, resulting in an element of randomness in the localised damage. This may in turn affect the global properties and failure parameters of components made of CFRPs. This raises the question of whether the inherent stochasticity of localised damage is of significance in terms of the global properties and design methods for such materials. This paper presents a numerical modelling based analysis of the effect of material randomness on delamination damage in CFRP materials by the implementation of a stochastic cohesive-zone model (CZM) within the framework of the finite-element (FE) method. The initiation and propagation of delamination in a unidirectional CFRP double-cantilever beam (DCB) specimen loaded under mode-I was analyzed, accounting for the inherent microstructural stochasticity exhibited by such laminates via the stochastic CZM. Various statistical realizations for a half-scatter of 50 % of fracture energy were performed, with a probability distribution based on Weibull's two-parameter probability density function. The damaged area and the crack lengths in laminates were analyzed, and the results showed higher values of those parameters for random realizations compared to the uniform case for the same levels of applied displacement. This indicates that deterministic analysis of composites using average properties may be non-conservative and a method based on probability may be more appropriate. © 2013 Springer Science+Business Media Dordrecht