Influence of adding multiwalled carbon nanotubes on the adhesive strength of composite epoxy/sol–gel materials

The tensile shear strength of a composite epoxy/sol–gel system modified with different ratios of multiwall carbon nanotubes (MWCNTs) was evaluated using a mechanical testing machine. The experimental results showed that the shear strength increased when lower than ~0.07 wt% of MWCNTs were added in the composite solution. The increase of the shear strength was attributed to both the mechanical load transfer from the matrix to the MWCNTs and the high specific surface area of this material that increased the degree of crosslinking with other inorganic fillers in the formulation. However, a decrease in the adhesive shear strength was observed after more than ~0.07 wt% MWCNTs were added to the composite. The reason for this may be related to the high concentration of MWCNTs within the matrix leading to excessively high viscosity, dewetting of the substrate surfaces, and reduced bonding of MWCNTs with the matrix, thereby limiting the strength. SEM observation of the fracture surfaces for composite epoxy/sol–gel adhesive materials with 0.01 wt% MWCNTs showed a mixed interfacial/cohesive fracture mode. This fracture mode indicated strong links at the adhesive/substrate interface, and interaction between CNTs and the matrix was achieved; therefore, adhesion performance of the composite epoxy/sol–gel material to the substrate was improved. An increase of a strong peak related to the C–O bond at ~1733 cm-1 in the FTIR spectra was observed. This peak represented crosslinking between the CNT surface and the organosilica nanoparticles in the MWCNTs-doped composite adhesive. Raman spectroscopy was also used to identify MWCNTs within the adhesive material. The Raman spectra exhibit peaks at ~1275 cm-1 and in the range of ~1549–1590 cm-1. The former is the graphite G-band, while the latter is the diamond D-band. The D-band and G-band represent the C–C single bond and C=C double bond in carbon nanotubes, respectively