Examination of weld defects by computed tomography
Defects in metal arc gas (MAG) welds made in S235JR low carbon steel of 6 mm thickness were examined. A sample containing lack of fusion (LOF) and pores was examined by computed tomography ā CT. The computed tomography examination was performed in order to define LOF size and position as well as dimensions and distribution of accompanying pores in the weld metal
Ispitivanje greŔaka zavara kompjutorskom tomografijom
Defects in metal arc gas (MAG) welds made in S235JR low carbon steel of 6 mm thickness were examined. A sample containing lack of fusion (LOF) and pores was examined by computed tomography ā CT. The computed tomography examination was performed in order to define LOF size and position as well as dimensions and distribution of accompanying pores in the weld metal.Ispitivane su greÅ”ke u zavarenom spoju niskougljiÄnog Äelika S235JR debljine 6 mm zavarenog MAG postupkom. Uzorak koji sadrži greÅ”ke naljepljivanja i pore je ispitivan kompjutorskom tomografijom - KT. Programskom analizom tomografa je odreÄena veliÄina i pozicija greÅ”aka naljepljivanja kao i dimenzije i raspored prateÄih pora u zavarenom spoju
Fracture of drilling head pipe connection due to quenching of heat affected zone (HAZ)
The drilling head pipe connection is made of quenched and tempered steel 34CrNiMo6. The steel characteristic is high hardenability. Due to unsuitable and untested welding technology the heat affected zone (HAZ) cooling rate after welding surpassed the upper critical cooling rate. During horizontal drilling of the rock, the resulting brittle martensite could not bear the dynamic loads which led to a brittle fracture of the pipe connection
Metallurgical reactions in the coalescence zone between a reinforcement and a base metal in reinforced brazed joints
Daily newspaper from Sapulpa, Oklahoma that includes local, state, and national news along with advertising
Reaktionen mit N-(1-Benzotriazolylcarbonyl)-aminosauren. I. Synthese von Hydantoinen und Hydantoinsaure-amiden
Die N-(1-Benzotriazolylcarbonyl)-aminosiiuren (I) werden mit
Thionylchlorid in die mit der BTCO-gruppe geschutzten Aminosiiure-
chloride (II) uberftihrt. Die konnen dann mit verschiedenen
Aminen, indirekt uber isolierbare N-(1-Benzotriazolylcarbonyl)-
aminosiiureamiden (III), oder direkt in die entsprechend substituierten
Hydantoinsiiure-amide (IV) umgesetzt werden.
Die Verbindungen III unterliegen bei der Einwirkung von
Alkalien einer Cyclisierungs-Eliminierungs-Reaktion und liefern
die 3,5-substituierte Hydantoine (V)
- ā¦