ВЛИЯНИЕ pH СРЕДЫ НА АНОДНОЕ ПОВЕДЕНИЕ СПЛАВА Zn55Al, ЛЕГИРОВАННОГО СКАНДИЕМ

The anodic behavior of Zn55Al alloy doped with scandium has been studied. The scandium content dependence of the Zn55Al alloy corrosion potential shows the extreme character. The increase in the chloride ion concentration in the electrolyte reduces the corrosion potential. When doping element content grows in the alloys, pitting and repassivation potentials are shifted to the positive area, and when chloride ion concentration grows, the potentials are shifted to the negative area over the entire range of environment pH. Zn55Al alloy corrosion rate decreases 2–3 times in doping 0,005–0,05 wt.% scandium. Thus the alloys of such composition can be recommended as anode coating for corrosion protection of steel structures, components, and constructions.Исследовано анодное поведение сплава Zn55Al, легированного скандием. Установлен экстремальный характер зависимости потенциала коррозии этого материала от содержания в нем Sc и показано, что увеличение концентрации хлорид-ионов в электролите способствует уменьшению потенциала коррозии. Потенциалы питтингообразования и репассивации с ростом содержания легирующих элементов в сплавах смещаются в положительную, а с увеличением концентрации хлорид-ионов в отрицательную область во всем интервале рН среды. Скорость коррозии Zn55Al уменьшается в 2–3 раза при добавке в него 0,005–0,05 мас.% Sc, что позволяет рекомендовать сплав такого состава в качестве анодного покрытия для защиты от коррозии стальных конструкций, изделий и сооружений