Acid Ionic Liquids as a New Hardener in Urea-Glyoxal Adhesive Resins

International audienceThe effect of acidic ionic liquid (IL) as a new catalyst on the properties of wood-based panels bonded with urea-glyoxal (UG) resins was investigated. Different levels of N-methyl-2-pyrrolidone hydrogen sulfate ([HNMP] HSO4 (0, 1, 2, 3 wt %)) were added to prepared UG resin. The resin was then used for preparing laboratory particleboard panels. Then, the properties of the prepared panels were evaluated. The structure of the prepared UG resin was studied by C-13 NMR, and thermal curing behavior of the resin before and after the addition of IL was measured by DSC. Additionally, the main oligomers formed in the UG reaction were identified by matrix-assisted laser desorption/ionization time-of-flight (MALDI TOF) mass spectroscopy. The results indicated that IL can be used as an efficient catalyst for UG resin. The physicochemical tests indicated that the addition of [HNMP] HSO4 from 0 to 3 wt % decreased the pH value of the glue-mix, and the pH decreased on curing to the same level as urea-formaldehyde resins. The gel accelerated with increasing catalyst content and with the decreasing of the pH in the UG resin. The panels prepared with IL had higher mechanical strength and dimensional stability compared to those made from UG resins containing NH4Cl. Scanning electron microscope (SEM) micrographs showed that the panels prepared with ionic liquid presented low porous. DSC analysis showed that the addition of IL to the UG resin decrease the energy of activation of the curing reaction to render possible cross-linking. The MALDI TOF results indicated a preponderant linearity of the oligomers formed, implying a high energy of activation of curing for UG resins

A Comparison among Lignin Modification Methods on the Properties of Lignin–Phenol–Formaldehyde Resin as Wood Adhesive

The research aim of this work is to determine the influence of lignin modification methods on lignin–phenol–formaldehyde (LPF) adhesive properties. Thus, glyoxal (G), phenol (P), ionic liquid (IL), and maleic anhydride (MA) were used to modify lignin. The modified lignins were used for phenol substitution (50 wt%) in phenol–formaldehyde adhesives. The prepared resins were then used for the preparation of wood particleboard. These LPF resins were characterized physicochemically, namely by using standard methods to determine gel time, solids content, density, and viscosity, thus the physicochemical properties of the LPF resins synthesized. The panels dimensional stability, formaldehyde emission, bending modulus, bending strength, and internal bond (IB) strength were also measured. MA-modified lignin showed by differential scanning calorimetry (DSC) the lowest temperature of curing than the resins with non-modified lignin and modified with IL, phenolared lignin, and glyoxal. LPF resins with lignin treated with maleic anhydride presented a shorter gel time, higher viscosity, and solids content than the resins with other lignin modifications. Equally, the particleboard panels prepared with LPF resins with maleic anhydride or with ionic liquid had the lowest formaldehyde emission and the highest mechanical strength among all the synthesized resins. The dimensional stability of all panels bonded with modified lignin LPF resins presented no difference of any significance

A comparison between lignin modified by ionic liquids and glyoxalated lignin as modifiers of urea-formaldehyde resin

International audienc

Reduction of Formaldehyde Emission from Particleboard by Phenolated Kraft Lignin

International audienceThe aim of this study was the reduction of formaldehyde emission from particleboard by phenolated Kraft lignin. For this purpose, the lignin was extracted from black liquor and then modified by phenolation. During the urea formaldehyde (UF) resin synthesis different proportions of unmodified and phenolated Kraft lignins (10%, 15%, and 20%) were added at pH = 7 instead of the second urea. Physicochemical properties and structural changes of resins so prepared, as well as the internal bond (IB) strength and formaldehyde emission associated with the panels bonded with them were measured according to standard methods. The Fourier transform infrared (FTIR) analysis of lignin indicated that the content of O-H bonds increased in phenolated lignin while the aliphatic ethers C-O bonds decreased markedly in the modified lignin. Since both synthesis of UF resins and lignin phenolation are carried out under acid conditions, phenolation is an interesting way of modifying lignin for use in wood adhesive. The panels bonded with these resins showed significantly lower formaldehyde emission compared to commercial UF adhesives. The UF resin with 20% phenolated lignin exhibited less formaldehyde release without significant differences in internal bond strength and physicochemical properties compared to an unmodified UF resin. XRD analysis results indicated that addition of phenolated lignin decreased the crystallinity of the hardened UF resins