By introducing the generalized uncertainty principle, we calculate the entropy of the bulk scalar field on the Randall-Sundrum brane background without any cutoff. We obtain the entropy of the massive scalar field proportional to the horizon area. Here, we observe that the mass contribution to the entropy exists in contrast to all previous results, which is independent of the mass of the scalar field, of the usual black hole cases with the generalized uncertainty principle.Comment: 12 pages. The improved version published in Phys. Rev.

Characterization of failure processes in tungsten copper composites under fatigue loading conditions

A fractographic and metallographic investigation was performed on specimens of a tungsten fiber reinforced copper matrix composite (9 vol percent), which had experienced fatigue failures at elevated temperatures. Major failure modes and possible failure mechanisms, with an emphasis placed on characterizing fatigue damage accumulation, were determined. Metallography of specimens fatigued under isothermal cyclic loading suggested that fatigue damage initiates in the matrix. Cracks nucleated within the copper matrix at grain boundaries, and they propagated through cavity coalescence. The growing cracks subsequently interacted with the reinforcing tungsten fibers, producing a localized ductile fiber failure. Examinations of interrupted tests before final failure confirmed the suggested fatigue damage processes