The improvement of GaN-based light-emitting diodes using nanopatterned sapphire substrate with small pattern spacing

Self-assembly SiO2 nanosphere monolayer template is utilized to fabricate nanopatterned sapphire substrates (NPSSs) with 0-nm, 50-nm, and 120-nm spacing, receptively. The GaN growth on top of NPSS with 0-nm spacing has the best crystal quality because of laterally epitaxial overgrowth. However, GaN growth from pattern top is more difficult to get smooth surface than from pattern bottom. The rougher surface may result in a higher work voltage. The stimulation results of finite-difference time-domain (FDTD) display that too large or too small spacing lead to the reduced light extracted efficiency (LEE) of LEDs. Under a driving current 350 mA, the external quantum efficiencies (EQE) of GaN-based LEDs grown on NPSSs with 0-nm, 50-nm, and 120-nm spacing increase by 43.3%, 50.6%, and 39.1%, respectively, compared to that on flat sapphire substrate (FSS). The optimized pattern spacing is 50 nm for the NPSS with 600-nm pattern period. (C) 2014 Author(s). All article content, except where otherwise noted, is licensed under a Creative Commons Attribution 3.0 Unported License

Phosphor-free nanopyramid white light-emitting diodes grown on {10(1)over-bar1} planes using nanospherical-lens photolithography

We reported a high-efficiency and low-cost nano-pattern method, the nanospherical-lens photolithography technique, to fabricate a SiO2 mask for selective area growth. By controlling the selective growth, we got a highly ordered hexagonal nanopyramid light emitting diodes with InGaN/GaN quantum wells grown on nanofacets, demonstrating an electrically driven phosphor-free white light emission. We found that both the quantum well width and indium incorporation increased linearly along the {10 (1) over bar1} planes towards the substrate and the perpendicular direction to the {10 (1) over bar1} planes as well. Such spatial distribution was responsible for the broadband emission. Moreover, using cathodoluminescence techniques, it was found that the blue emission originated from nanopyramid top, resembling the quantum dots, green emission from the InGaN quantum wells layer at the middle of sidewalls, and yellow emission mainly from the bottom of nanopyramid ridges, similar to the quantum wires.We reported a high-efficiency and low-cost nano-pattern method, the nanospherical-lens photolithography technique, to fabricate a SiO2 mask for selective area growth. By controlling the selective growth, we got a highly ordered hexagonal nanopyramid light emitting diodes with InGaN/GaN quantum wells grown on nanofacets, demonstrating an electrically driven phosphor-free white light emission. We found that both the quantum well width and indium incorporation increased linearly along the {10 (1) over bar1} planes towards the substrate and the perpendicular direction to the {10 (1) over bar1} planes as well. Such spatial distribution was responsible for the broadband emission. Moreover, using cathodoluminescence techniques, it was found that the blue emission originated from nanopyramid top, resembling the quantum dots, green emission from the InGaN quantum wells layer at the middle of sidewalls, and yellow emission mainly from the bottom of nanopyramid ridges, similar to the quantum wires. (C) 2013 AIP Publishing LLC

Nanospherical-lens lithographical Ag nanodisk arrays embedded in p-GaN for localized surface plasmon-enhanced blue light emitting diodes

Large-scale Ag nanodisks (NDs) arrays fabricated using nanospherical-lens lithography (NLL) are embedded in p-GaN layer of an InGaN/GaN light-emitting diode (LED) for generating localized surface plasmon (LSP) coupling with the radiating dipoles in the quantum-well (QWs). Based on the Ag NDs with the controlled surface coverage, LSP leads to the improved crystalline quality of regrowth p-GaN, increased photoluminescence (PL) intensity, reduced PL decay time, and enhanced output power of LED. Compared with the LED without Ag NDs, the optical output power at a current of 350 mA of the LSP-enhanced LEDs with Ag NDs having a distance of 20 and 35 nm to QWs is increased by 26.7% and 31.1%, respectively. The electrical characteristics and optical properties of LEDs with embedded Ag NPs are dependent on the distance of between Ag NPs and QWs region. The LED with Ag NDs array structure is also found to exhibit reduced emission divergence, compared to that without Ag NDs. (C) 2014 Author(s). All article content, except where otherwise noted, is licensed under a Creative Commons Attribution 3.0 Unported License

Fabrication and optical characteristics of phosphor-free InGaN nanopyramid white light emitting diodes by nanospherical-lens photolithography

A novel nanopattern technique of nanospherical-lens photolithography is introduced to fabricate the InGaN nanopyramid white (NPW) light-emitting diodes (LEDs) by selective area growth. Highly ordered NPW LED arrays are achieved after optimizing the growth conditions. It is found that the NPW LEDs vary from warm white light to cool with the increase in growth temperature. For the cool white NPW LEDs, the spectrum is similar to the conventional white LEDs obtained from the blue LEDs combined with yellow phosphors. The blue emission originates from the upper sidewalls of nanopyramids, and yellow light is mainly emitted from the lower ridges with respect to the base of nanopyramids. Furthermore, simulation shows that the light extraction efficiency of NPW LEDs is about 4 times higher compared with conventional ones, and the escape cone is as much as 85 degrees due to their three-dimensional nanopyramid structures. These observations suggest that the proposed phosphor-free NPW LEDs may have great potential for highly efficient white lighting. (C) 2014 AIP Publishing LLC