Low-Temperature Sensitization Behavior of Base, Heat-Affected Zone, and Weld Pool in AISI 304LN
Present investigations were focused on low-temperature sensitization (LTS) behavior of 304LN stainless steels considered from pipes of two different thicknesses. The specimens for the present study were taken from solution-annealed pipes (of varying thicknesses) and welded pipes (including the heat-affected zone (HAZ)). The specimens were subjected to thermal aging at 400 °C and 450 °C for different durations ranging from 125 to 8000 hours, to evaluate their sensitization susceptibility. The aging durations were worked out to simulate the 30-to-100-year life of the studied stainless steel at 300 °C using the Arrheneous equation and considering the activation energy of 150 kJ/mol. The thermally aged specimens were characterized for their degree of sensitization (DOS) and susceptibility to intergranular corrosion (IGC) by double-loop (DL) electrochemical potentiokinetic reactivation (EPR) and by methods given in the ASTM A262 practices A and E. It has been clearly shown that the weld pool is more sensitive to IGC than are the base and the HAZ at both the aging temperatures (LTS), because they showed IGC cracks during the bending subsequent to the boiling in H2SO4-CuSO4 solution. Both the base and the HAZ of the thicker pipe material showed susceptibility to sensitization, as indicated by the increasing DOS and “dual-type” microstructure during electrolytic oxalic acid (EOA) etching; however, they were found safe from IGC for the studied sensitization times. The susceptibility to sensitization and IGC in the weld pool is related to the presence of copious delta ferrite with chromium diffusivity that is accelerated compared to the austenite phase. The time-temperature-sensitization (TTS) curves were prepared accordingly, based on these results